EPO-TEK® 353ND-LH Ultra
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 30lmoH_EPO-TEK-353ND-LH-Ultra.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A two component, high temperature epoxy designed for semiconductor, hybrid, fiber optic and medical applications. This product easily meets halogen-free requirements. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Ion Type | |||
| Cl- | 38 | ppm | |
| K+ | 0 | ppm | |
| Na+ | 1 | ppm | |
| NH4+ | 386 | ppm |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Degradation Temperature | 418 | °C | |
| Operating Temperature | |||
| Continuous | -55 to 250 | °C | |
| Intermittent | -55 to 350 | °C | |
| Storage Modulus | 3.24 | GPa | |
| Weight Loss on Heating | |||
| 200°C | 0.050 | % | |
| 250°C | 0.18 | % | |
| 300°C | 0.58 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature | 102 | °C | |
| CLTE - Flow | |||
| -- 1 | 4.4E-5 | cm/cm/°C | |
| -- 2 | 1.9E-4 | cm/cm/°C |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Refractive Index 3 | 1.567 | ||
| Transmittance (860 to 1600 nm) | > 98.0 | % |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 10 | ||
| Part B | Mix Ratio by Weight: 1.0 | ||
| Shelf Life (23°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | |||
| -- 4 | Amber | ||
| -- 5 | Clear/Transparent | ||
| Density | |||
| Part B | 1.02 | g/cm³ | |
| Part A | 1.19 | g/cm³ | |
| Viscosity 6(23°C) | 3.7 | Pa·s | |
| Curing Time (150°C) | 0.017 | hr | |
| Pot Life | < 180 | min |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness (Shore D) | 85 | ||
| Lap Shear Strength (23°C) | > 13.8 | MPa |
| Note Message | |
|---|---|
| 1 . | Below Tg |
| 2 . | Above Tg |
| 3 . | 589 nm |
| 4 . | Part B |
| 5 . | Part A |
| 6 . | 50 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYNIL® P125 | Nilit Plastics | Nylon 66 | POLYNIL® |
| PRL PC-BR1 | Polymer Resources Ltd. | PC | PRL |
| Westlake PVC 1230P | Westlake Chemical Corporation | PVC, Rigid | Westlake PVC |
| New-prene™ 9175N | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| MACOMASS PP MM-PP HK 23 | MACOMASS Verkaufs AG | PP Homopolymer | MACOMASS PP |