Durethan® BKV 130 H2.0 DUS008 901510
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 30MNr4_DurethanBKV130H20DUS008901510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 30 % glass fibers, injection molding, improved impact strength, heat-aging stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.36 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction : 280°C, 2.00mm 1 | 0.80 | -- | % | ISO 294-4 |
| Vertical flow direction : 120°C, 2 hours, 2.00mm 2 | 0.10 | -- | % | ISO 294-4 |
| Flow direction : 280°C, 2.00mm 3 | 0.30 | -- | % | ISO 294-4 |
| Flow direction : 120°C, 2 hours, 2.00mm 4 | 0.10 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 6.6 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 9300 | 5200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 160 | 100 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.4 | 8.0 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 8600 | 4700 | MPa | ISO 178/A |
| Flexural Stress 6 | ||||
| 3.5% strain | 240 | 125 | MPa | ISO 178/A |
| 23°C | 250 | 155 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 7(23°C) | 4.3 | 6.7 | % |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6-HI, GHR, 14-090, GF30 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Films | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Film Puncture Energy | ISO 6603-2 | |||
| -- 8 | 2.50 | -- | J | ISO 6603-2 |
| -- 9 | 4.30 | -- | J | ISO 6603-2 |
| Film Puncture Force | ISO 6603-2 | |||
| -- 10 | 765 | -- | N | ISO 6603-2 |
| -- 11 | 990 | -- | N | ISO 6603-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | < 10 | < 10 | kJ/m² | ISO 179/1eA |
| 23°C | 13 | 20 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 75 | 75 | kJ/m² | ISO 179/1eU |
| 23°C | 90 | 90 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | < 10 | < 10 | kJ/m² | ISO 180/1A |
| 23°C | 15 | 22 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 70 | 70 | kJ/m² | ISO 180/1U |
| 23°C | 80 | 85 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 218 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 202 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 212 | -- | °C | ISO 306/B120 |
| Melting Temperature 12 | 221 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 2.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 1.0E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 260 - 290 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2; MT 80°C; 600 Bar |
| 2 . | 60x60x2 |
| 3 . | 60x60x2; MT 80°C; 600 Bar |
| 4 . | 60x60x2 |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Pull Rate: 2 mm/min; 50% RH |
| 8 . | -30°C |
| 9 . | 23°C |
| 10 . | -30°C |
| 11 . | 23°C |
| 12 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® A9845 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Ultramid® T 4381 LDS | BASF Corporation | Nylon 6/6T | Ultramid® |
| Argothane® 46510 | Argotec LLC | TPU, Unspecified | Argothane® |
| EnCom M20 PBET | EnCom, Inc. | Polyester, TP | EnCom |
| LNP™ STAT-KON™ DEL22P compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |