Vyncolit® BXE650
| Category: | Phenolic , Phenolic |
| Manufacturer: | Vyncolit N.V. |
| Trademark: | Vyncolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 30ItGg_Vyncolit-BXE650.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vyncolit® BXE650 is an inorganic filled phenolic molding compound with excellent isotropic properties, superior dimensional stability . It is specially used for potable water applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.99 | g/cm³ | ISO 1183 |
| Apparent Density | 0.73 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.20 | % | ISO 2577 |
| Water Absorption (Saturation, 23°C) | 0.040 | % | ISO 62 |
| Post Shrinkage | 0.040 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain at Break | 1.2 | % | ISO 178 |
| Tensile Modulus | 23000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 120 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.67 | % | ISO 527-2 |
| Flexural Modulus | 21000 | MPa | ISO 178 |
| Flexural Stress | 247 | MPa | ISO 178 |
| Compressive Stress | 431 | MPa | ISO 604 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.54 | ||
| vs. Itself - Static | 0.56 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.8 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 15 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | > 250 | °C | ISO 75-2/Af |
| 8.0 MPa, Unannealed | 178 | °C | ISO 75-2/Cf |
| CLTE | TMA | ||
| Flow | 1.6E-5 | cm/cm/°C | |
| Transverse | 2.4E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.51 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.5E+12 | ohms | IEC 60093 |
| Volume Resistivity | 2.1E+14 | ohms·cm | IEC 60093 |
| Electric Strength | 17 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Retpol® 7555 HS UV2 | PolyPacific Pty. Ltd. | PP, Unspecified | Retpol® |
| Vi-Chem PVC V220-80E | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Cellophane™ 335MSC | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Comco PA 6 G MOS 2 | Comco-Plastic GmbH | Nylon 6 | Comco |
| ISORENE™ FA9-1101 | SABIC Innovative Plastics Europe | TPE | ISORENE™ |