ebalta GH 761/D is a very well castable two-components epoxy casting resin, which even cures at 40 mm thickness at room temperature. The excellent castability allows versatile applications as a massive casting resin. During processing just note that the extremely low-viscosity hardener is mixed carefully with the filled resin. The resin/hardener mixture has a long potlife and is well castable free from air bubbles. Applications
Properties
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Shore Hardness (Shore D) | 87 to 93 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 8200 to 9500 | MPa | ISO 178 |
| Flexural Stress | 80.0 to 90.0 | MPa | ISO 178 |
| Compressive Stress | 100 to 120 | MPa | ISO 604 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 57.0 to 61.0 | °C | ISO 75-2/B |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 5.0 | ||
| Resin | Mix Ratio by Weight: 100 |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 2.40 to 2.50 | g/cm³ | |
| Viscosity (25°C) | 2.0 to 3.0 | Pa·s | |
| Curing Time (20°C) | 14 to 16 | hr | |
| Pot Life 1(20°C) | 50 to 60 | min |
| Note Message | |
|---|---|
| 1 . | 200 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP Semitron® ESd 520HR | Quadrant Engineering Plastic Products | PTFE | Quadrant EPP |
| SCHULAMID® 6 GF 30 HI WIT | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| EPT 8110 | Mitsui Chemicals, Inc. | EPDM | EPT |
| Jiangsu Meilan XXMLF2-12 | Jiangsu Meilan Chemical Co., Ltd. | Fluorelastomer | Jiangsu Meilan |
| LNP™ LUBRICOMP™ UFL269SA compound | SABIC Innovative Plastics | PPA | LNP™ LUBRICOMP™ |