INSTRUC PA66GF10IM

Category:	Nylon 66 , Polyamide 66
Manufacturer:	Infinity LTL Engineered Compounds
Trademark:	INSTRUC
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	2yz3QI_INSTRUC-PA66GF10IM.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Instruc glass and carbon fiber reinforced, mineral and process additive filled structural compounds - Offered in all Infinity base resins

Provide significant improvements in strength, stiffness, creep resistance, fatigue endurance and impact & dimensional stability

Increased thermal HDTUL and long term heat resistance

General Information
Filler / Reinforcement	Glass Fiber, 10% Filler by Weight
Additive	Impact Modifier
Features	Fatigue Resistant Good Creep Resistance Good Dimensional Stability Good Heat Aging Resistance Good Impact Resistance High Stiffness High Strength Impact Modified Medium Heat Resistance
Uses	Structural Parts

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.16	g/cm³	ASTM D792
Specific Volume	0.863	cm³/g
Molding Shrinkage - Flow	0.60 to 1.0	%	ASTM D955
Water Absorption (24 hr)	1.1	%	ASTM D570

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Yield)	72.4	MPa	ASTM D638
Tensile Elongation (Yield)	8.0 to 9.0	%	ASTM D638
Flexural Modulus	2760	MPa	ASTM D790
Flexural Strength	103	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (3.18 mm)	180	J/m	ASTM D256
Unnotched Izod Impact (3.18 mm)	750	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	238	°C	ASTM D648
CLTE - Flow	6.5E-5	cm/cm/°C	ASTM D696

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+16	ohms	ASTM D257

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.59 mm)	HB		UL 94

Injection	Nominal Value	Unit
Drying Temperature	79.4	°C
Drying Time	4.0	hr
Processing (Melt) Temp	260 to 302	°C
Mold Temperature	93.3	°C
Back Pressure	0.345 to 0.689	MPa
Screw Speed	40 to 70	rpm
Vent Depth	0.013 to 0.025	mm

Resin Grade	Manufacturer	Category	Trademark
Cheng Yu T-66	Cheng Yu Plastic Company Limited	Nylon 66	Cheng Yu
LNP™ KONDUIT™ PX10323 compound	SABIC Innovative Plastics Europe	Nylon 6	LNP™ KONDUIT™
Lucent PP TPP-310	Lucent Polymers, Inc.	PP, Unspecified	Lucent PP
Petrothene® GA501026	LyondellBasell Industries	LLDPE	Petrothene®
Sylvin 3250-80 Black	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin