CYCOLOY™ NX07353 resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2xuBtp_CYCOLOY-NX07353-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CYCOLOY C7230P resin is a mineral filled, flame retardant PC/ABS. Good stiffness combined with balanced flow and impact performance, makes it a good candidate for various applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/2.16 kg) | 13 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 9.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.25 to 0.35 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.090 | % | |
| Equilibrium, 23°C, 50% RH | 0.040 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 5190 | MPa | ASTM D638 |
| -- | 5580 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 55.0 | MPa | ASTM D638 |
| Yield | 55.0 | MPa | ISO 527-2/50 |
| Break 3 | 43.0 | MPa | ASTM D638 |
| Break | 35.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 4.0 | % | ASTM D638 |
| Yield | 3.8 | % | ISO 527-2/50 |
| Break | 30 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 5 | 4530 | MPa | ASTM D790 |
| -- 6 | 4580 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 99.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 7 | 95.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 8(23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 48 | J/m | ASTM D256 |
| 23°C | 65 | J/m | ASTM D256 |
| -30°C 9 | 5.0 | kJ/m² | ISO 180/1A |
| 23°C 10 | 5.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 88.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 89.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 108 | °C | ASTM D1525 12 |
| -- | 107 | °C | ISO 306/B50 |
| -- | 110 | °C | ISO 306/B120 |
| CLTE | |||
| Flow : -40 to 40°C | 4.2E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Transverse : -40 to 40°C | 4.9E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 5.9E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.20 mm | V-0 | ||
| 2.00 mm | 5VB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 87.8 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Shot Size | 30 to 80 | % | |
| Rear Temperature | 221 to 254 | °C | |
| Middle Temperature | 221 to 266 | °C | |
| Front Temperature | 243 to 277 | °C | |
| Nozzle Temperature | 243 to 277 | °C | |
| Processing (Melt) Temp | 243 to 277 | °C | |
| Mold Temperature | 60.0 to 82.2 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.038 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 sp=62mm |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMTOUGH RZ220 | Polyram Ram-On Industries | PC | RAMTOUGH |
| Capa™ 6400 | Perstorp Holding AB | PCL | Capa™ |
| EPO-TEK® 731 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| SEQUEL® 1493-UV NH533 | LyondellBasell Industries | PP, Unspecified | SEQUEL® |
| TOPAS® 6013M-07 | Topas Advanced Polymers, Inc. | COC | TOPAS® |