CALIBRE™ 701-15
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2xkU6V_CALIBRE-701-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ 701-15 Series resins are formulated and produced to supply both clarity and enhanced ignition resistance. They do so while maintaining excellent physical properties and processability. The CALIBRE 701-15 series products are available in 2 additive packages: CALIBRE 701: Mold release. CALIBRE 703: Mold release and UV stabilizer. Main Characteristics
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | |||
| -- | 1.20 | g/cm³ | ISO 1183/A |
| -- | 1200 | kg/m³ | ISO 1183 1 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 15 | g/10 min | ISO 1133 |
| Melt volume-flow rate (300°C/1.2 kg) | 12.0 | cm³/10min | ISO 1133 2 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ISO 294-4 |
| Water Absorption | ISO 62 3 | ||
| Saturation | 0.030 | % | |
| Equilibrium | 0.23 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2/50, ISO 527-2 3 4 |
| Tensile Stress | |||
| Yield | 60.0 | MPa | ISO 527-2/50, ISO 527-2 5 |
| Break | 66.0 | MPa | ISO 527-2/50 |
| Tensile Strain | |||
| Yield | 6.0 | % | ISO 527-2/50, ISO 527-2 6 |
| Break | 120 | % | ISO 527-2/50 |
| Nominal strain at break | > 50 | % | ISO 527-2 7 |
| Flexural Modulus | 2400 | MPa | ISO 178 |
| Flexural Stress | 100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23°C | 20 | kJ/m² | ISO 179/1eA |
| -30°C | 15.0 | kJ/m² | ISO 179/1eA 8 |
| 23°C | 17.0 | kJ/m² | ISO 179/1eA 9 |
| Charpy impact strength | ISO 179/1eU 10 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength (23°C) | 83 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 142 | °C | ISO 75-2/B |
| 0.45 MPa | 140 | °C | ISO 75-2 11 |
| 1.8 MPa, Unannealed | 122 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 139 | °C | ISO 75-2/A |
| 1.8 MPa | 122 | °C | ISO 75-2 12 |
| Vicat Softening Temperature | |||
| -- | 147 | °C | ISO 306/B50 |
| 50°C/h, B (50N) | 147 | °C | ISO 306 13 |
| Ball Indentation Temperature | 125 | °C | IEC 60335-1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | |||
| 2.00 mm, Solution A | 250 | V | IEC 60112 |
| -- | 250 | IEC 60112 14 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 15 | UL 94 | ||
| 1.60 mm | V-2 | ||
| 3.20 mm | V-0 | ||
| Burning Behav. at 1.6mm nom. thickn. (1.60 mm, UL) | V-2 | ISO 1210 16 | |
| Burning Behav. at thickness h (3.20 mm, UL) | V-0 | ISO 1210 17 |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 10 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 11 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 12 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 13 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 14 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 15 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 16 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 17 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Razalen® Q111 GR30 | Razin™ Engineering Plastics | PP Homopolymer | Razalen® |
| ASTALAC™ ASA 309 | Marplex Australia Pty. Ltd. | ASA | ASTALAC™ |
| Ateva® 2030 | Celanese EVA Performance Polymers | EVA | Ateva® |
| Hax™ HF 039/4H | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |
| Hifax CB 1160 G1 BLACK | LyondellBasell Industries | PP Copolymer | Hifax |