INSULCAST® RTVS 8128
| Category: | Silicone Rubber, RTV-2 , Silicone Rubber, RTV-2 |
| Manufacturer: | ITW Polymers Coatings North America |
| Trademark: | INSULCAST® RTVS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2wylxy_INSULCAST-RTVS-8128.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| RTVS 8128 is a low viscosity Flame Retardant, general purpose, reversion resistant RTV Silicone. With the ability to cure rapidly at elevated temperature, RTVS 8128 combines the virtues of low temperature flexibility, excellent electrical properties, high temperature resistance and easy removal for component replacement or repair. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 52 to 58 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 3.45 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 140 | % | ASTM D412 |
| Tear Strength 1 | 3.15 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| CLTE - Flow | 2.2E-4 | cm/cm/°C | |
| Thermal Conductivity | 0.31 | W/m/K | |
| Service Temperature | -55 to 204 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.5E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 22 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 3.00 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 7.0E-3 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Volume: 1.0 Mix Ratio by Weight: 1.0 | ||
| Part B | Mix Ratio by Volume: 1.1 Mix Ratio by Weight: 1.0 | ||
| Shelf Life (25°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 2 | Colorless | ||
| -- 3 | Grey | ||
| Density | |||
| -- 4 | 1.31 | g/cm³ | |
| -- 5 | 1.38 | g/cm³ | |
| Viscosity | ASTM D2393 | ||
| -- 6 | 2.0 | Pa·s | |
| -- 7 | 2.0 | Pa·s | |
| -- 8 | 2.0 | Pa·s | |
| Curing Time | |||
| 120°C | 0.25 | hr | |
| 90°C | 1.0 | hr | |
| 60°C | 4.0 | hr | |
| 25°C | 24 | hr | |
| Gel Time (25°C) | 2.4E+2 to 3.6E+2 | min | |
| Pot Life (25°C) | 60 to 90 | min |
| Note Message | |
|---|---|
| 1 . | Die B |
| 2 . | Part B |
| 3 . | Part A |
| 4 . | Part B |
| 5 . | Part A |
| 6 . | Mixed |
| 7 . | Part B |
| 8 . | Part A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Menzolit® SMC 2600 | Menzolit Ltd (UK) | Polyester, TS | Menzolit® |
| Fainplast PVC PM 7010/K | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| HANWHA CHBA-880FR | Hanwha Chemical | Polyolefin, Unspecified | HANWHA |
| Kumho KTR KTR-201 | Korea Kumho Petrochemical Co., Ltd. | SBS | Kumho KTR |
| Luran® 378P G10 | Styrolution | SAN | Luran® |