Order Products : sales@su-jiao.com
TECHNYL® C 402 M NATURAL
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2tbDIa_TECHNYL-C-402-M-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unreinforced polyamide PA6, high viscosity, containing monomer, for extrusion. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183/A |
| Water Absorption (23°C, 24 hr) | 1.9 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 1200 | 550 | MPa | ISO 527-2/1A |
| Tensile Stress (Yield) | 55.0 | 35.0 | MPa | ISO 527-2/1A |
| Flexural Modulus | 1000 | 530 | MPa | ISO 178 |
| Flexural Stress | 50.0 | 30.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 18 kJ/m² | No Break | ISO 179/1eA | |
| Charpy Unnotched Impact Strength | No Break | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength | 15 kJ/m² | No Break | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 65.0 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 222 | -- | °C | ISO 11357-3 |
| CLTE - Flow (23 to 85°C) | 7.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+11 | ohms·cm | IEC 60093 |
| Electric Strength | -- | 18 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.60 | 4.10 | IEC 60250 | |
| Dissipation Factor | 0.020 | 0.12 | IEC 60250 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 225 to 230 | °C | |
| Middle Temperature | 230 to 240 | °C | |
| Front Temperature | 235 to 245 | °C | |
| Mold Temperature | 40.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® 8272G HS BK-102 | BASF Corporation | Nylon 6 | Ultramid® |
| ELIX™ ABS P2L-AT | ELIX Polymers, S. L. | ABS | ELIX™ ABS |
| Hypro® PPH-GF10 NATURAL | Entec Polymers | PP Homopolymer | Hypro® |
| Braskem PE HD9601C | Braskem | HDPE | Braskem PE |
| LNP™ STAT-KON™ EE004 compound | SABIC Innovative Plastics | PEI | LNP™ STAT-KON™ |