Desmopan® 460
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Desmopan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2szSKh_Desmopan-460.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| injection molding grade; grease and oil-resistant; low compression set; good heat resistance; high elasticity; short cycle times; Application; Automotive engineering; Technical parts; Bearing bushes |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1220 | kg/m³ | ISO 1183 1 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 2 | ||
| Shore A, 3 sec | 97 | ||
| Shore D, 15 sec | 59 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 3 | DIN 53504 | ||
| Break, 23°C | 42.5 | MPa | |
| 10% Strain, 23°C | 15.1 | MPa | |
| 50% Strain, 23°C | 22.5 | MPa | |
| 300% Strain, 23°C | 35.1 | MPa | |
| Tensile Strain 4(Break, 23°C) | 390 | % | DIN 53504 |
| Flexural Modulus 5 | 170 | MPa | ISO 178 |
| Abrasion Resistance (23°C) | 40.0 | mm³ | ISO 4649-A |
| Tensile Storage Modulus | ISO 6721-1,-4 | ||
| -20°C | 1.76 | GPa | |
| 20°C | 0.446 | GPa | |
| 60°C | 0.130 | GPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Resilience | 35 | % | ISO 4662 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 6 | 150 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 25 | % | |
| 70°C, 24 hr | 35 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 110 | °C | |
| Processing (Melt) Temp | 235 to 245 | °C | |
| Mold Temperature | 20.0 to 40.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | 200 mm/min |
| 4 . | 200 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nycal™ 1850RMC40H | Technical Polymers, LLC | Nylon 6 | Nycal™ |
| FM® 309-1 | Cytec Industries Inc. | Adhesive | FM® |
| LNP™ THERMOCOMP™ RF007ES compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| MAJORIS DW305 - 8090 | AD majoris | PP, Unspecified | MAJORIS |
| Hostacom EBS 777D White | LyondellBasell Industries | Polyolefin, Unspecified | Hostacom |