Order Products : sales@su-jiao.com
QR Resin QR-1220
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | QTR, Inc. |
| Trademark: | QR Resin |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2su944_QR-Resin-QR-1220.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Available with UV (V) or Release (R). |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 55.2 | MPa | ASTM D638 |
| Flexural Modulus | 2310 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 86.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 530 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 104 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 107 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 246 to 282 | °C | |
| Middle Temperature | 249 to 293 | °C | |
| Front Temperature | 260 to 299 | °C | |
| Nozzle Temperature | 271 to 299 | °C | |
| Processing (Melt) Temp | 249 to 293 | °C | |
| Mold Temperature | 60.0 to 87.8 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SZF4569 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Spartech Polycom PP5150 | Spartech Polycom | PP Homopolymer | Spartech |
| Bergamid™ A70 G15 TM-Z | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Fiberfil® J-69/10/E | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| KOPLA PA66 KDT1040 | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |