LNP STAT-KON* MD000 is a compound based on Polypropylene resin containing Carbon Powder. Added feature of this material is: Electrically Conductive. Also known as: LNP* STAT-KON* Compound M Product reorder name: MD000 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.950 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 1.3 to 1.6 | % | ASTM D955 |
| Across Flow : 24 hr | 1.3 to 1.6 | % | ASTM D955 |
| Across Flow : 24 hr | 1.3 | % | ISO 294-4 |
| Flow : 24 hr | 1.5 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.030 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.030 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1250 | MPa | ASTM D638 |
| -- | 1220 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 21.9 | MPa | ASTM D638 |
| Yield | 21.5 | MPa | ISO 527-2 |
| Break | 16.9 | MPa | ASTM D638 |
| Break | 16.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 8.4 | % | ASTM D638 |
| Yield | 6.3 | % | ISO 527-2 |
| Break | 48 | % | ASTM D638 |
| Break | 52 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 1180 | MPa | ASTM D790 |
| -- | 1160 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 29.2 | MPa | ASTM D790 |
| -- | 24.9 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 820 | J/m | ASTM D256 |
| 23°C 2 | 60 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812, ISO 180/1U | |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 33.4 | J | ASTM D3763 |
| -- | 32.8 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 51.7 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 3 | 53.0 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.0E-4 | cm/cm/°C | |
| Transverse : -40 to 40°C | 1.0E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 216 to 227 | °C | |
| Front Temperature | 238 to 249 | °C | |
| Processing (Melt) Temp | 227 to 249 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUSTARIN® C GLD 160 | Röchling Sustaplast SE & Co. KG | Acetal (POM) Copolymer | SUSTARIN® |
| Monprene® IN-12990 | Teknor Apex Company | TPE | Monprene® |
| Adell PBT HD-30 | Adell Plastics, Inc. | PBT | Adell PBT |
| Eastar™ DN114, Natural | Eastman Chemical Company | Copolyester | Eastar™ |
| Kepex® 3320GVS | Korea Engineering Plastics Co., Ltd | PBT | Kepex® |