OmniLon™ PA6 U BK1000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | OMNI Plastics, LLC |
| Trademark: | OmniLon™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2sUGpp_OmniLon-PA6-U-BK1000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Utility Grade, Nylon 6 |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Molding Shrinkage | 0.012 to 2.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3100 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 72.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 40 | % | ASTM D638 |
| Flexural Modulus | 2620 | MPa | ASTM D790 |
| Flexural Strength | 107 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 177 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 65.6 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.18 mm) | HB | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 232 to 271 | °C | |
| Middle Temperature | 238 to 271 | °C | |
| Front Temperature | 238 to 271 | °C | |
| Nozzle Temperature | 249 to 282 | °C | |
| Processing (Melt) Temp | 232 to 271 | °C | |
| Mold Temperature | 26.7 to 82.2 | °C | |
| Back Pressure | 0.345 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RANPELEN SFC-851 | Lotte Chemical Corporation | PP Terpolymer | RANPELEN |
| SABIC® PP 522L | Saudi Basic Industries Corporation (SABIC) | PP Homopolymer | SABIC® PP |
| SUMIKASUPER® LCP E6807LHF | Sumitomo Chemical Co., Ltd. | LCP | SUMIKASUPER® LCP |
| LNP™ THERMOTUF™ QX01581H compound | SABIC Innovative Plastics Asia Pacific | Nylon 610 | LNP™ THERMOTUF™ |
| Alathon® M5265X01 | LyondellBasell Industries | HDPE | Alathon® |