Sup-tech P240
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Shanghai Suptech Engineering Plastics Co. Ltd. |
| Trademark: | Sup-tech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2rQQYv_Sup-tech-P240.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sup-tech P240 is a Polypropylene product filled with 30% mineral. It can be processed by injection molding and is available in Asia Pacific. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | DIN 53479 |
| Melt Mass-Flow Rate (MFR) | 2.0 to 8.0 | g/10 min | DIN 53735 |
| Molding Shrinkage | 0.014 | % | DIN 53464 |
| Water Absorption (23°C, 24 hr) | 0.030 | % | DIN 53495 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 85 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 34.0 | MPa | DIN 53455 |
| Tensile Strain (Break) | 10 | % | DIN 53452 |
| Flexural Modulus | 2500 | MPa | DIN 53457 |
| Flexural Stress | 45.0 | MPa | DIN 53457 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.0 | kJ/m² | DIN 53453 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | DIN 53461 | ||
| 0.45 MPa, Unannealed | 125 | °C | |
| 1.8 MPa, Unannealed | 90.0 | °C | |
| Melting Temperature | 165 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Electric Strength | 19 | kV/mm | DIN 53481 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 185 to 240 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYSTONE® D black AST | Röchling Engineering Plastics SE & Co. KG | HMWPE | POLYSTONE® |
| RJM SN504 | RJM International, Inc. | Nylon 6 | RJM |
| SIVIC® 620 | SIDIAC | PVC+NBR | SIVIC® |
| Vydyne® R530H BK0202 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Exelene® LLDPE 1801 | Montachem International, Inc. | LLDPE | Exelene® LLDPE |