Makrolon® 8325
| Category: | PC , Polycarbonate |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Makrolon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2rLg6Z_Makrolon-8325.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MVR (300 °C/1.2 kg) 4.0 cm³/10 min; 20 % glass fiber reinforced; high viscosity; easy release; injection molding - melt temperature 310 - 330 °C; extrusion; available in opaque colors only |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.34 | g/cm³ | ISO 1183 |
| Apparent Density 1 | 0.64 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 5.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 4.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Across Flow | 0.30 to 0.50 | % | ISO 2577 |
| Flow | 0.30 to 0.50 | % | ISO 2577 |
| Across Flow : 2.00 mm 2 | 0.45 | % | ISO 294-4 |
| Flow : 2.00 mm 3 | 0.35 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.24 | % | |
| Equilibrium, 23°C, 50% RH | 0.10 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 144 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 5800 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield, 23°C | 99.0 | MPa | ISO 527-2/50 |
| Break, 23°C | 85.0 | MPa | ISO 527-2/5 |
| Tensile Strain | |||
| Yield, 23°C | 3.3 | % | ISO 527-2/50 |
| Break, 23°C | 4.4 | % | ISO 527-2/5 |
| Flexural Modulus 4(23°C) | 5300 | MPa | ISO 178 |
| Flexural Stress 5 | ISO 178 | ||
| 3.5% Strain, 23°C | 145 | MPa | |
| 23°C | 150 | MPa | |
| Flexural Strain at Flexural Strength 6(23°C) | 4.5 | % | ISO 178 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flash Ignition Temperature | 470 | °C | ASTM D1929 |
| Self Ignition Temperature | 550 | °C | ASTM D1929 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| ISO Shortname | ISO 7391-PC,MR,(,,)-05-5,GF20 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 7(23°C, Complete Break) | 10 | kJ/m² | ISO 7391 |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -60°C, Complete Break | 65 | kJ/m² | |
| -30°C, Complete Break | 65 | kJ/m² | |
| 23°C, Complete Break | 60 | kJ/m² | |
| Notched Izod Impact Strength 8(23°C, Complete Break) | 10 | kJ/m² | ISO 7391 |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | ||
| -30°C | 5.00 | J | |
| 23°C | 5.00 | J | |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | ||
| -30°C | 1000 | N | |
| 23°C | 1000 | N |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 145 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 142 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 149 | °C | ISO 306/B50 |
| -- | 150 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 3.0E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 6.5E-5 | cm/cm/°C | |
| Thermal Conductivity 9(23°C) | 0.23 | W/m/K | ISO 8302 |
| RTI Elec (1.50 mm) | 80.0 | °C | UL 746 |
| RTI Imp (1.50 mm) | 80.0 | °C | UL 746 |
| RTI Str (1.50 mm) | 80.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength (23°C, 1.00 mm) | 36 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.30 | ||
| 23°C, 1 MHz | 3.30 | ||
| Dissipation Factor | IEC 60250 | ||
| 23°C, 100 Hz | 1.0E-3 | ||
| 23°C, 1 MHz | 9.0E-3 | ||
| Comparative Tracking Index | IEC 60112 | ||
| Solution A | 175 | V | |
| Solution B | 125 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-2 | ||
| 3.00 mm | V-0 | ||
| Oxygen Index 10 | 32 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Pellets |
| 2 . | 60x60x2 mm, 500 bar |
| 3 . | 60x60x2 mm, 500 bar |
| 4 . | 2.0 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 2 mm/min |
| 7 . | Based on ISO 179-1eA, 3 mm |
| 8 . | Based on ISO 180-A, 3 mm |
| 9 . | Cross-flow |
| 10 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BCC Resins BC 100 Thick | BCC Products Inc. | EA | BCC Resins |
| Colorite SF 6811SF | Colorite Polymers | PVC, Unspecified | Colorite SF |
| Ferro PP TPP20AA11BK | Ferro Corporation | PP Homopolymer | Ferro PP |
| Latene® 7H2W TR/40 | LATI S.p.A. | PP Homopolymer | Latene® |
| Kumho PS HI 425TVL | Korea Kumho Petrochemical Co., Ltd. | PS (HIPS) | Kumho PS |