Vitaster® UY36BK6435
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | Vitaster® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2qmGW9_Vitaster-UY36BK6435.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vitaster® UY36BK6435 is a Polybutylene Terephthalate (PBT) product filled with 30% glass fiber. It is available in Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.59 | g/cm³ | ASTM D792, ISO 1183 |
| Water Absorption (23°C, 24 hr) | 0.030 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 115 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.5 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 8500 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 180 | MPa | ISO 178 |
| Break | 180 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 10 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 220 | °C | ASTM D648, ISO 75-2/B |
| Melting Temperature | 225 | °C | ISO 1218, ASTM D2117 |
| CLTE - Flow | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | 20 | kV/mm | ASTM D149, IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Medalist® MD-115A | Teknor Apex Company | TPE | Medalist® |
| TAROBLEND 66 | Taro Plast S.p.A. | PC+ABS | TAROBLEND |
| DENKA EVA TEX 100 | Denka Company Limited | EVA | DENKA EVA TEX |
| Hyundai EP PA66 LD240 | HYUNDAI EP Co., Ltd. | Nylon 66 | Hyundai EP PA66 |
| apilon 52® MA-6505 | API SpA | TPU-Polyester | apilon 52® |