LEXAN™ EXRL1061 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2qlk6n_LEXAN-EXRL1061-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Transparent Polycarbonate in natural color. Excellent processability, super high flow. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 260°C/2.16 kg | 23 | g/10 min | |
| 300°C/1.2 kg | 45 | g/10 min | |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 43.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 to 0.80 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.28 | % | |
| Equilibrium, 23°C, 50% RH | 0.35 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2850 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 75.0 | MPa | |
| Break | 55.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 5.0 | % | |
| Break | 60 | % | |
| Flexural Modulus 1 | 2750 | MPa | ISO 178 |
| Flexural Stress | 110 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2 | ISO 179/1eA | ||
| -30°C | 5.6 | kJ/m² | |
| 23°C | 5.7 | kJ/m² | |
| Charpy Unnotched Impact Strength 3 | ISO 179/1eU | ||
| -30°C | > 100 | kJ/m² | |
| 23°C | > 100 | kJ/m² | |
| Notched Izod Impact | |||
| -30°C | 45 | J/m | ASTM D256 |
| 23°C | 40 | J/m | ASTM D256 |
| -30°C 4 | 5.7 | kJ/m² | ISO 180/1A |
| 23°C 5 | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 6 | ISO 180/1U | ||
| -30°C | > 100 | kJ/m² | |
| 23°C | > 100 | kJ/m² | |
| Instrumented Dart Impact (23°C, Total Energy) | 80.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 98.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 7 | 101 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 108 | °C | ASTM D1525 8 |
| -- | 107 | °C | ISO 306/B50 |
| -- | 110 | °C | ISO 306/B120 |
| CLTE | |||
| Flow : -40 to 40°C | 6.6E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 7.2E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 6.7E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 80°C | 7.4E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 230 to 250 | °C | |
| Middle Temperature | 240 to 260 | °C | |
| Front Temperature | 250 to 270 | °C | |
| Nozzle Temperature | 240 to 260 | °C | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 70.0 to 85.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*3 sp=62mm |
| 3 . | 80*10*3 sp=62mm |
| 4 . | 80*10*3 |
| 5 . | 80*10*3 |
| 6 . | 80*10*3 |
| 7 . | 80*10*4 mm |
| 8 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds HM-304 (Comp) | Ravago Manufacturing Americas, LLC | MDPE | Ravago Compounds |
| VESTAMID® HTplus R1033 | Evonik Industries AG | PPA | VESTAMID® HTplus |
| GAPEX® APP40GR30HB GRAY | Ferro Corporation | PP Homopolymer | GAPEX® |
| Huaxia Shenzhou PFA DS708-C | Shandong Huaxia Shenzhou New Material Co., Ltd. | PFA | Huaxia Shenzhou |
| MAJ'ECO EN000LA | AD majoris | Biodeg Polymers | MAJ'ECO |