MAJORIS ET212 - 8229
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2plK1F_MAJORIS-ET212---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ET212 - 8229 is a mineral filled polypropylene compound intended for injection moulding. The product is available in natural (ET212) but other colours can be provided on request. ET212 - 8229 has a very easy flowing and excellent mechanical properties. APPLICATIONS Products requiring good long term heat resistance, very high heat distortion temperature, excellent rigidity, low shrinkage and high dimensional stability such as :
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 12 | g/10 min | ISO 1133 |
| 230°C/5.0 kg | 60 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.1 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 88.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 31.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 38 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2600 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 1.1 | kJ/m² | ISO 179/1eA |
| 23°C | 2.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 14 | kJ/m² | ISO 179/1eU |
| 23°C | 32 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 124 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 70.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 155 | °C | ISO 306/A |
| -- | 99.0 | °C | ISO 306/B |
| Thermal stability (150°C) | > 700.0 | hr |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Fogging | DIN 75201 | ||
| 100°C/16h | 2.0E-4 | g | DIN 75201 |
| 100°C/3h | 97 | % | DIN 75201 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emission | 22.0 | µgC/g | VDA 277 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure. |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Retpol® 7572 | PolyPacific Pty. Ltd. | PP, Unspecified | Retpol® |
| KPOL-NYLON K-NY66/21VCF | KPOL Chem Co. | Nylon 66 | KPOL-NYLON |
| PermaStat® 1800 Nat/Clear | RTP Company | Acrylic (PMMA) | PermaStat® |
| SD POLYCA™ 878-20 | Sumika Styron Polycarbonate Limited | PC | SD POLYCA™ |
| Stat-Tech™ ST6000-5006 FR BLACK X3 | PolyOne Corporation | Nylon 6 | Stat-Tech™ |