LNP™ KONDUIT™ PX09322 compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ KONDUIT™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2pkwbG_LNP-KONDUIT-PX09322-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| White colored thermally conductive mineral filled PA6 FR compound |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.52 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal Method | ||
| Flow | 0.58 | % | |
| Across Flow | 0.53 | % | |
| Water Absorption (24 hr, 50% RH) | 0.060 | % | ASTM D570 |
| UV Weathering - Start F1 from 1mm onword | PASSES | UL 746C | |
| Water Immersion - Start F1 from 1mm onword | PASSES | UL 746C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 10400 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 51.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 0.80 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 11000 | MPa | ASTM D790 |
| Flexural Strength 5 | ASTM D790 | ||
| Yield, 50.0 mm Span | 80.0 | MPa | |
| Break, 50.0 mm Span | 81.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 22 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 130 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 210 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 182 | °C | |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 2.4E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 3.7E-5 | cm/cm/°C | |
| Thermal Conductivity | |||
| -- 6 | 1.5 | W/m/K | ASTM E1461 |
| -- 7 | 6.0 | W/m/K | ASTM E1461 |
| -- 8 | 0.86 | W/m/K | ISO 22007-2 |
| -- 9 | 2.7 | W/m/K | ISO 22007-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 8.1E+14 | ohms | ASTM D257 |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.20 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Rear Temperature | 230 to 270 | °C | |
| Middle Temperature | 240 to 280 | °C | |
| Front Temperature | 250 to 280 | °C | |
| Nozzle Temperature | 250 to 280 | °C | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Back Pressure | 0.300 to 0.900 | MPa | |
| Screw Speed | 30 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | through-plane, 10*10*3mm sample |
| 7 . | in-plane, ø25*0.4mm disc |
| 8 . | through-plane, ø80*3mm discs |
| 9 . | in-plane, ø80*3mm discs |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| KOPA® KN333HB38BL | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| Sylvin 3220-85 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| OTECH PVC OW132 - Wire Jacket | OTECH Corporation | PVC, Unspecified | OTECH PVC |
| Kepital® F40-03 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| Moplen EP440M | PolyMirae | PP Impact Copolymer | Moplen |