LNP™ THERMOCOMP™ DF0029P compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2p39dn_LNP-THERMOCOMP-DF0029P-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* DF0029P is a compound based on Polycarbonate resin containing 10% Glass Fiber. Added features of this material include: Exceptional Processing. Flame Retardant. Also known as: LNP* THERMOCOMP* Compound DF-1002 EP FR Product reorder name: DF0029P |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.40 | % | ASTM D955 |
| Across Flow : 24 hr | 0.40 | % | ASTM D955 |
| Across Flow : 24 hr | 0.48 | % | ISO 294-4 |
| Flow : 24 hr | 0.42 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4620 | MPa | ASTM D638 |
| -- | 4800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 92.9 | MPa | ASTM D638 |
| Break | 93.2 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 3.8 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 4690 | MPa | ASTM D790 |
| -- | 5000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 155 | MPa | ASTM D790 |
| -- | 159 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 43 | J/m | ASTM D256 |
| 23°C 2 | 5.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 410 | J/m | ASTM D4812 |
| 23°C 3 | 33 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 5.30 | J | ASTM D3763 |
| -- | 1.44 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 141 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 136 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 134 | °C | ISO 75-2/Af |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.640 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Diaterm® A27 10 | DTR S.r.l. (Develop Thermoplastic Resins) | Nylon 6 | Diaterm® |
| Flontech® FLON-0122-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Hifax DG 232 2693 | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |
| Hapflex™ 570 | Hapco Inc. | TP, Unspecified | Hapflex™ |
| Sylvin 916VO-90 Grey 9459 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |