Milastomer™ M4400NS
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Mitsui Chemicals America, Inc. |
| Trademark: | Milastomer™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2mPPBS_Milastomer-M4400NS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Milastomer™M4400NS is a thermoplastic vulcanized rubber (TPV) material,. This product is available in North America and is processed by extrusion. Milastomer™Typical application fields of M4400NS are: engineering/industrial accessories |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.890 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.50 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 5 sec) | 46 | ISO 48 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1(100% Strain) | 10.4 | MPa | ISO 37 |
| Tensile Stress 2(Break) | 17.8 | MPa | ISO 37 |
| Tensile Elongation 3(Break) | 650 | % | ISO 37 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -60.0 | °C | Internal method |
| Additional Information |
|---|
| All tests performed according to Mitsui methods. |
| Note Message | |
|---|---|
| 1 . | 500 mm/min |
| 2 . | 500 mm/min |
| 3 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Selvol™ 523S | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| Chemlon® 109 HU | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| DynaChar™ 3544 | Polymer Dynamix | Polyolefin, Unspecified | DynaChar™ |
| INNOPOL® PP CS 1-3140 MA | Inno-Comp Ltd. | PP Homopolymer | INNOPOL® PP |
| OnForce™ LFT PP-50LGF/001 UV Black | PolyOne Corporation | PP Homopolymer | OnForce™ LFT |