Plexar® PX3080
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Plexar® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2lorMg_Plexar-PX3080.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Plexar® tie-layers are chemically modified resins used to bond unlike materials, primarily in packaging and industrial applications. Common adherents include polyethylene resins and copolymers, such as EVA or EMA, polypropylene, polyamide (nylon), ethylene vinyl alcohol copolymers (EVOH), ionomer and other sealants, polyethylene terephthalate (PET) resins and copolymers, styrenic polymers, metal, paper and many others. Product grades tailored for blown and cast films, sheet and thermoforming, blow molding, extrusion coating and lamination, tubing, pipe, spray coating and other specialty applications are available in pellet form. |
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.8 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm, Blown Film | 8.80 | MPa | |
| TD : Yield, 51 µm, Blown Film | 9.70 | MPa | |
| MD : Break, 51 µm, Blown Film | 22.8 | MPa | |
| TD : Break, 51 µm, Blown Film | 22.2 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Yield, 51 µm, Blown Film | 16 | % | |
| TD : Yield, 51 µm, Blown Film | 7.0 | % | |
| MD : Break, 51 µm, Blown Film | 790 | % | |
| TD : Break, 51 µm, Blown Film | 800 | % | |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm, Blown Film | 840 | g | |
| TD : 51 µm, Blown Film | 1300 | g | |
| Water Vapor Transmission Rate (100% RH, 51 µm, Blown Film) | 8.9 | g/m²/24 hr | ASTM F372 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 98.0 | °C | ASTM D1525 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | > 210 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8200-85 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 8329-65D Natural | Sylvin Technologies Incorporated | PVC, Semi-Rigid | Sylvin |
| Ultramid® B3GM35 BKQ649 23220 | BASF Corporation | Nylon 6 | Ultramid® |
| LARIPUR® LPR 5925 | COIM S.p.A. | TPU-Polyester | LARIPUR® |
| Karina MBU ORANGE E 32/214-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |