LNP™ THERMOCOMP™ AF002 compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2lmgBe_LNPTHERMOCOMPAF002compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP AF002 is a compound based on ABS resin containing 10% Glass Fiber. UL rating applicable for NC color only. Also known as: LNP* THERMOCOMP* Compound AF-1002 Product reorder name: AF002 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.10 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.20 - 0.40 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.33 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3600 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 54.0 | MPa | ISO 527-2/5 |
| Fracture | 54.0 | MPa | ISO 527-2/5 |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 2.7 | % | ISO 527-2/5 |
| Fracture | 2.8 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 3500 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| -- 3 | 83.0 | MPa | ISO 178 |
| -- 4 | 59.0 | MPa | ISO 178 |
| Flexural Strain at Break 5 | 3.7 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 6(23°C) | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 7(23°C) | 21 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 8 | |||
| 0.45 MPa, unannealed, 64.0mm span | 102 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 95.0 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 - 0.10 | % | |
| Rear Temperature | 204 - 216 | °C | |
| Middle Temperature | 232 - 243 | °C | |
| Front Temperature | 266 - 277 | °C | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 71.1 - 82.2 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Yield |
| 4 . | Break |
| 5 . | 2 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan A-9016/B-8016 | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyester | Xuchuan |
| Bapolan® PS6445 | Bamberger Polymers, Inc. | PS (HIPS) | Bapolan® |
| BJB Polyurethane TC-890 A/B | BJB Enterprises, Inc. | PUR, Unspecified | BJB Polyurethane |
| LNP™ THERMOCOMP™ MF008GS compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ THERMOCOMP™ |
| OTECH PVC OE9213 - Profile | OTECH Corporation | PVC, Unspecified | OTECH PVC |