POLYabs H00
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Polykemi AB |
| Trademark: | POLYabs |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2lNa2x_POLYabs-H00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Heat resistant |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/5.0 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.60 to 0.80 | % | |
| Flow | 0.60 to 0.80 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 47.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 6.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2300 | MPa | ISO 178 |
| Flexural Stress | 82.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 8.0 | kJ/m² | |
| 23°C | 16 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1 | |||
| 0.45 MPa, Unannealed | 100 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 84.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 124 | °C | ISO 306/A50 |
| -- | 110 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NOVADURAN® 5010G45 | Mitsubishi Engineering-Plastics Corp | PBT | NOVADURAN® |
| Nylene® KH 5133-HSL | Custom Resins Group | Nylon 66 | Nylene® |
| Alkathene® WNC199 | Qenos Pty Ltd | LLDPE | Alkathene® |
| Electrafil® TPX-HTN-01045 A | Techmer Engineered Solutions | Nylon, Unspecified | Electrafil® |
| Osterlene® PPC10-2.1 | Osterman & Company | PP Impact Copolymer | Osterlene® |