CALIBRE™ 301V-6
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2l7vrd_CALIBRE-301V-6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ 301V-6 Polycarbonate resin offers exceptional impact resistance and heat distortion resistance, and meets UL94 V-2 rating. CALIBRE 301V-6 contains a mold release agent and is available in opaque colors. Govt. and Industry Standards:
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 6.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.50 - 0.70 | % | ASTM D955 |
| Flow direction | 0.50 - 0.70 | % | ISO 294-4 |
| Water Absorption | ASTM D570, ISO 62 | ||
| 23°C, 24 hr | 0.15 | % | ASTM D570, ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.32 | % | ASTM D570, ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| Class m | 73 | ASTM D785 | |
| Class r | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2410 | MPa | ASTM D638 |
| -- | 2410 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 60.0 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 72.4 | MPa | ASTM D638 |
| Fracture | 72.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 6.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Fracture 5 | 150 | % | ASTM D638 |
| Fracture | 150 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 6 | 2410 | MPa | ASTM D790 |
| -- | 2410 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 96.5 | MPa | ASTM D790 |
| -- | 96.0 | MPa | ISO 178 |
| Taber Abrasion Resistance | 45 | % | ASTM D1044 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Average Extent of Burning | 3 | cm | ASTM D635 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 910 | J/m | ASTM D256 |
| 23°C | 88 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact (23°C) | No Break | ASTM D256, ISO 180 | |
| Instrumented Dart Impact 8(23°C, Total Energy) | 90.4 | J | ASTM D3763 |
| Tensile Impact Strength | 588 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, annealed | 142 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, not annealed | 122 | °C | ASTM D648, ISO 75-2/A |
| 1.8 MPa, annealed | 139 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 148 | °C | ISO 306/B50, ASTM D1525 9 |
| CLTE - Flow (-40 to 82°C) | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength | 17 | kV/mm | ASTM D149, IEC 60243-1 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 3.00 | ASTM D150 | |
| 1 MHz | 3.00 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 1.0E-3 | ASTM D150 | |
| 1 MHz | 2.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 10 | UL 94 | ||
| 1.60 mm | V-2 | UL 94 | |
| 3.20 mm | V-2 | UL 94 | |
| Oxygen Index 11 | 26 | % | ISO 4589-2 |
| Additional Information |
|---|
| ASTM 和 ISO 测试方法在技术上可能不相同，所以数据值可能不同于简单单位换算获得的值。 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 50 mm/min |
| 6 . | Method I (three-point load), 2.0 mm/min |
| 7 . | Method I (three-point load), 2.0 mm/min |
| 8 . | 3.39 m/sec |
| 9 . | 速率 A (50°C/h), 载荷2 (50N) |
| 10 . | This rating is not intended to reflect the danger caused by this or any other material under actual fire conditions. |
| 11 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P2950 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Sylvin 2957-80 White 1534 | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| Visico™ LE4421/LE4432 | Borealis AG | Polyolefin, Unspecified | Visico™ |
| APEX® 55303 | Teknor Apex Company | PVC, Flexible | APEX® |
| NILAMID® XS1 GF60 | Nilit Plastics | Nylon, Unspecified | NILAMID® |