LNP™ STAT-KON™ RD000I compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2keNLN_LNP-STAT-KON-RD000I-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON RD000I is a compound based on Nylon 66 resin containing Carbon Powder. Added features of this material include: Electrically Conductive, High Impact. Also known as: LNP* STAT-KON* Compound R-HI Product reorder name: RD000I |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 2.0 to 4.0 | % | |
| Across Flow : 24 hr | 2.0 to 4.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.49 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.73 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2120 | MPa | ASTM D638 |
| -- | 2190 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 41.0 | MPa | ASTM D638 |
| Break | 41.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 18 | % | ASTM D638 |
| Break | 18 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 1920 | MPa | ASTM D790 |
| -- 5 | 2030 | MPa | ISO 178 |
| Flexural Stress | 62.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 140 | J/m | ASTM D256 |
| 23°C 6 | 15 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1800 | J/m | ASTM D4812 |
| 23°C 7 | 160 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 16.2 | J | ASTM D3763 |
| -- | 20.9 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 206 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 8 | 191 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 71.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 9 | 68.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 1.1E-4 | cm/cm/°C | |
| Transverse : -30 to 30°C | 1.2E-4 | cm/cm/°C | |
| Thermal Conductivity | 2.8 | W/m/K | ASTM E1530 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| 9 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Baydur® 665 IBS (35 pcf) | Covestro - PUR | PUR-MDI | Baydur® |
| Alkathene® Ultra LDH210 | Qenos Pty Ltd | LLDPE | Alkathene® Ultra |
| DESLON™ 6 DSC102GK | DESCO Co., Ltd. | Nylon 6 | DESLON™ 6 |
| LEXAN™ EXL8454 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| Karina ICE PVC COMPOUND 651D28/29-D-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |