SABIC® LLDPE 6135NE
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2kMPsw_SABIC-LLDPE-6135NE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LLDPE 6135NE is a hexene linear low density polyethylene resin. Films made from this resin exhibit a good balance between mechanical properties (like impact strength, tear strength and hottack) and optical properties on the one hand and stiffness on the other hand. Application Typical applications for SABIC® LLDPE 6135NE are heavy duty bags, lamination films, agriculture films, frozen food packaging and other applications requiring a balance between high impact strength, tear resistance and stiffness. The grade is typically used for multi layer recipes. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.932 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 50 µm, blown film | 310 | MPa | ISO 527-3 |
| TD : 50 µm, blown film | 360 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 50 µm, blown film | 16.0 | MPa | ISO 527-3 |
| TD : Yield, 50 µm, blown film | 19.0 | MPa | ISO 527-3 |
| MD : Broken, 50 µm, blown film | 53.0 | MPa | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 50.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | 700 | % | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 850 | % | ISO 527-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength - Blown Film (50.0 µm) | 70.0 | J/cm | ASTM D4272 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Blocking - Blown Film (50.0 µm) | g | Internal method | |
| Puncture Resistance - Blown Film (50.0 µm) | 700 | J/m | Internal method |
| Tear Strength 1 | ISO 6383-2 | ||
| MD : 50.0 µm | 40.0 | kN/m | ISO 6383-2 |
| TD : 50.0 µm | 210.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 120 | °C | ISO 306/A |
| Melting Temperature (DSC) | 126 | °C | Internal method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film of 50 µm and BUR = 2 has been produced on Kuhne BF line with an output of 35 kg/h. Die size 120 mm, die gap 2.7 mm. |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Titalon® 2200ST | Titan Plastics Compounds Co., Ltd. | Nylon 66 | Titalon® |
| NEXUS PP HPP2 | Nexus Resin Group, LLC. | PP Homopolymer | NEXUS PP |
| Accura® ClearVue™ Free (SL 7870) | 3D Systems | Epoxy | Accura® |
| Hylon® N1013HL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| Hostacom TRC 454N G14008 | LyondellBasell Industries | PP Copolymer | Hostacom |