Order Products : sales@su-jiao.com
MarFlex® 9659
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Chevron Phillips Chemical Company LLC |
| Trademark: | MarFlex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2kF7Rw_MarFlex-9659.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MarFlex®9659 is a high density polyethylene material,. This product is available in North America or Latin America. The processing method is: blow molding film or co-extrusion molding. MarFlex®The main features of the 9659 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.962 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | 0.25 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm, blown film | 1080 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, blown film | 1370 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 42.0 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 26.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 490 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 550 | % | ASTM D882 |
| Oxygen Transmission Rate (25 µm, Blown Film) | 2000 | cm³/m²/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate (25 µm, Blown Film) | 4.0 | g/m²/24 hr | ASTM F1249 |
| Dart Drop Test - Blown Film (25.4 µm) | 19.3 | kN/m | ASTM D1709 |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 25.4 µm | 7.3 | kN/m | ASTM D1922 |
| TD : 25.4 µm | 81.1 | kN/m | ASTM D1922 |
| Additional Information |
|---|
| Blown Film produced using a grooved feed extruder, 8 lb/in die, 2.5 BUR, using a dual lip air ring. |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong Aobang TPU-Capro 90-A | Shandong Aobang Chemical Technology Co.,Ltd. | TPU-Capro | Shandong Aobang TPU-Capro |
| SPESIN® KP212G30V0BLS | Kolon Plastics, Inc. | PBT | SPESIN® |
| Vi-Chem PVC VNC107I | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| DIC.PPS FZ-2100 | DIC Corporation | PPS | DIC.PPS |
| Sylvin 9085-95 BLACK | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |