Bayfill® 382 (53.2:100) Datasheet,PUR-MDI,Covestro

Message
Bayfill 382 is a semi-rigid polyurethane foam system designed for automotive interior applications. The Bayfill 382 system is an excellent choice for the production of soft-touch panels, such as instrument panels, door trim, and center consoles. The foam is typically molded in a back-filling process between a soft, exterior skin and a rigid, thermoplastic substrate. The Bayfill 382 system is supplied as two components. Component A is a polymeric diphenylmethane diisocyanate (PMDI). Component B is a polyol mixture. As with any product, use of the Bayfill 382 system in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.

General Information
Uses	Foam Application in Automobile Field Car interior parts Car interior equipment Car dashboard

Physical	Nominal Value	Unit	Test Method
Molded Density	141	kg/m³	ASTM D3574A

Elastomers	Nominal Value	Unit	Test Method
Compression Force Deflection			ASTM D3574C
-- ¹	0.228	MPa	ASTM D3574C
-- ²	0.172	MPa	ASTM D3574C
Compression Set			ASTM D3574D
Cd ³	59	%	ASTM D3574D
Cd ⁴	51	%	ASTM D3574D
Ct ⁵	26	%	ASTM D3574D
Ct ⁶	30	%	ASTM D3574D

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength
-- ⁷	0.331	MPa	ASTM D3574K
--	0.352	MPa	ASTM D3574E
Tensile Elongation
Fracture ⁸	23	%	ASTM D3574K
Fracture	27	%	ASTM D3574E

Elastomers	Nominal Value	Unit	Test Method
Tear Strength	0.350	kN/m	ASTM D3574F

Thermoset	Nominal Value
Thermoset Components
Component a	Mixing ratio by weight: 53
Component B	Mixing ratio by weight: 100

Additional Information
Part A Type: Isocyanate Appearance: Dark brown to black liquid Specific Gravity @ 25°C: 1.24 Viscosity @25°C: 200 cps Flash Point PMCC: 199°C NCO: 31 wt% Part B Type: Polyol Appearance: Black liquid Specific Gravity @ 25°C: 1.01 Viscosity @25°C: 1400 cps Flash Point PMCC: 131°C Water: 2.8 wt% Hydroxyl Number: 70 KOH/g Material Temperatures: 27 to 32°CMold Temperature: 38 to 43°CDemold Time: >90 secHand Mix Reactivity at 25°C Cream Time: 14 to 22 sec Top of Cup Time: 50 to 64 sec Gel Time: 60 to 76 sec Rise Time: 87 to 107 sec Free-Rise Density: 2.9 to 4.5 lb/ft³ Machine Reactivity at 29°C Cream Time: 8 to 12 sec Top of Cup Time: 24 to 30 sec Gel Time: 40 to 45 sec Rise Time: 60 to 65 sec Free-Rise Density: 3.10 to 4.10 lb/ft³ Molded Density: 8.0 to 11.0 lb/ft³

Additional Information

Part A Type: Isocyanate Appearance: Dark brown to black liquid Specific Gravity @ 25°C: 1.24 Viscosity @25°C: 200 cps Flash Point PMCC: 199°C NCO: 31 wt% Part B Type: Polyol Appearance: Black liquid Specific Gravity @ 25°C: 1.01 Viscosity @25°C: 1400 cps Flash Point PMCC: 131°C Water: 2.8 wt% Hydroxyl Number: 70 KOH/g Material Temperatures: 27 to 32°CMold Temperature: 38 to 43°CDemold Time: >90 secHand Mix Reactivity at 25°C Cream Time: 14 to 22 sec Top of Cup Time: 50 to 64 sec Gel Time: 60 to 76 sec Rise Time: 87 to 107 sec Free-Rise Density: 2.9 to 4.5 lb/ft³ Machine Reactivity at 29°C Cream Time: 8 to 12 sec Top of Cup Time: 24 to 30 sec Gel Time: 40 to 45 sec Rise Time: 60 to 65 sec Free-Rise Density: 3.10 to 4.10 lb/ft³ Molded Density: 8.0 to 11.0 lb/ft³

Note Message
1 .	0.5
2 .	After J2 Autoclave
3 .	After J2 Autoclave, Cd=compression set as a percentage of the original deflection
4 .	50, Cd=compression set as a percentage of the original deflection
5 .	50%, Ct=compression set as a percentage of the original thickness
6 .	After J2 Autoclave, Ct=compression set as a percentage of the original thickness
7 .	Dry Heat Aged at 140°C
8 .	Dry Heat Aged at 140°C

Category:	PUR-MDI , Polyurethane (MDI)
Manufacturer:	Covestro - PUR
Trademark:	Bayfill®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	2k7RNQ_Bayfill-382-53-2-100-.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
NuSil CF-4721	NuSil Technology	Silicone	NuSil
DOWLEX™ 2056G	The Dow Chemical Company	LLDPE	DOWLEX™
LNP™ LUBRILOY™ DX08333 compound	SABIC Innovative Plastics Asia Pacific	PC	LNP™ LUBRILOY™
Lucky Enpla LGF3201FA	Lucky Enpla Co LTD	PC+PBT	Lucky Enpla
LUVOCOM® 1105-8052/EM/BL VP	Lehmann & Voss & Co.	PEEK	LUVOCOM®