Order Products : sales@su-jiao.com
SABIC® PC PC4800 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | SABIC® PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2gwQL7_SABIC-PC-PC4800-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC4800 resin is a very high flow (MFR = 8.0 at 250C/1.2kg) polycarbonate product designed for use in the optical media market. It is available exclusively at www.sabicpc.com. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/1.2 kg) | 8.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (250°C/1.2 kg) | 7.50 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.50 to 0.70 | % | Internal Method |
| Water Absorption | |||
| Saturation, 23°C | 0.35 | % | ISO 62 |
| Equilibrium, 23°C | 0.35 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 2350 | MPa | ASTM D638 |
| -- | 2350 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 60.0 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 6.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Break 5 | > 40 | % | ASTM D638 |
| Break | > 40 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2300 | MPa | ASTM D790 |
| -- 7 | 2300 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 90.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 90.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 9 | ISO 180/1A | ||
| -30°C | 12 | kJ/m² | |
| 23°C | 15 | kJ/m² | |
| Unnotched Izod Impact Strength 10 | ISO 180/1U | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 132 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 132 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 122 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 122 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 138 | °C | ISO 306/B50, ASTM D1525 13 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE - Flow | |||
| -40 to 95°C | 7.0E-5 | cm/cm/°C | ASTM E831 |
| 23 to 80°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.20 | W/m/K | ASTM C177, ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 3.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.010 | IEC 60250 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ASTM D542, ISO 489 | |
| Transmittance (2540 µm) | > 90.0 | % | ASTM D1003 |
| Haze (2540 µm) | < 0.70 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 270 to 290 | °C | |
| Middle Temperature | 320 to 340 | °C | |
| Front Temperature | 350 to 380 | °C | |
| Nozzle Temperature | 340 to 370 | °C | |
| Processing (Melt) Temp | 340 to 370 | °C | |
| Mold Temperature | 75.0 to 95.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*3 |
| 10 . | 80*10*3 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| 13 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® BR13NT6530 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Viton® B-600 | DuPont Performance Elastomers | Fluorelastomer | Viton® |
| Fainplast PVC PK 8020 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Geon™ Vinyl Flexible 90042 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Sylvin 9812-65 Red 6312 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |