UNIPA® Ld Datasheet,Nylon 66,Nytef Plastics, Ltd.-SHANGHAI SUSHENG

UNIPA® Ld

Category:	Nylon 66 , Polyamide 66
Manufacturer:	Nytef Plastics, Ltd.
Trademark:	UNIPA®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	2glcd8_UNIPA-Ld.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Since its introduction in 1938, Nylon has become one of the world's most widely recognized and utilized engineering grade thermoplastics. Nylon's unique combination of high strength, good toughness, outstanding chemical resistance, and excellent wear and abrasion resistance have made it the material of choice for product designs in a multitude of industries. When used to replace wear grade metals like brass and bronze, no other material provides the combination of extended wear life, light weight, and low fabricated part cost of Nylon. Nytef Plastics, Ltd. manufactures UNIPA® Nylon stock shapes in a wide variety of types and stock shape configurations. These UNIPA Nylon products fall into the categories of Type 6/6 Extruded UNIPA Nylons and Type 6 UNIPA M Cast Nylons. While both types of Nylon are very similar, there are performance and availability differences between the two grades that should be noted: UNIPA Type 6/6 Extruded Nylons: offer improved toughness offer improved flame resistance are available in smaller rod diameters (< 2" dia.) Nytef Plastic's UNIPA Nylon 6/6 extruded stock shapes are available in a wide range of grades— including both lubricated and fiber reinforced products. UNIPA Nylon 6/6 materials are offered in a complete range of extruded round, square, and hex rod, heavy gauge plate, and tubular bar sizes.

Message

Since its introduction in 1938, Nylon has become one of the world's most widely recognized and utilized engineering grade thermoplastics. Nylon's unique combination of high strength, good toughness, outstanding chemical resistance, and excellent wear and abrasion resistance have made it the material of choice for product designs in a multitude of industries. When used to replace wear grade metals like brass and bronze, no other material provides the combination of extended wear life, light weight, and low fabricated part cost of Nylon. Nytef Plastics, Ltd. manufactures UNIPA® Nylon stock shapes in a wide variety of types and stock shape configurations. These UNIPA Nylon products fall into the categories of Type 6/6 Extruded UNIPA Nylons and Type 6 UNIPA M Cast Nylons. While both types of Nylon are very similar, there are performance and availability differences between the two
grades that should be noted:

UNIPA Type 6/6 Extruded Nylons:

offer improved toughness

offer improved flame resistance

are available in smaller rod diameters (< 2" dia.)

Nytef Plastic's UNIPA Nylon 6/6 extruded stock shapes are available in a wide range of grades— including both lubricated and fiber reinforced products. UNIPA Nylon 6/6 materials are offered in a complete range of extruded round, square, and hex rod, heavy gauge plate, and tubular bar sizes.

General Information
Additive	Molybdenum Disulfide Lubricant
Features	Flame Retardant Good Abrasion Resistance Good Chemical Resistance Good Toughness Good Wear Resistance High Stiffness High Strength Lubricated Machinable
Uses	Automotive Applications Bearings Bushings Construction Applications Electrical Parts Electrical/Electronic Applications Fluid Handling Food Service Applications Gears Mining Applications Molds/Dies/Tools Pulleys Pump Parts Rollers Textile Applications Valves/Valve Parts Wear Strip Wheels
Appearance	Dark Grey
Forms	Preformed Parts Rod

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.16	g/cm³	ASTM D792
Water Absorption			ASTM D570
24 hr	0.70	%
Saturation	6.5	%

Hardness	Nominal Value	Test Method
Rockwell Hardness		ASTM D785
M-Scale	85
R-Scale	115

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	3450	MPa	ASTM D638
Tensile Strength	81.4	MPa	ASTM D638
Tensile Elongation (Break)	50	%	ASTM D638
Flexural Modulus	3310	MPa	ASTM D790
Flexural Strength	103	MPa	ASTM D790
Compressive Strength	110	MPa	ASTM D695
Coefficient of Friction	0.23		ASTM D1894

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	43	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	98.9	°C	ASTM D648
Continuous Use Temperature	98.9	°C	Internal Method
Peak Melting Temperature	257	°C	ASTM D3418
CLTE - Flow	7.2E-5	cm/cm/°C	ASTM D696

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	1.0E+13	ohms·cm	ASTM D257
Dielectric Strength ¹	14	kV/mm	ASTM D149
Dielectric Constant (60 MHz)	3.70		ASTM D150

Flammability	Nominal Value	Unit	Test Method
Flame Rating	V-2		UL 94

Note Message
1 .	Method A (Short-Time)

Resin Grade	Manufacturer	Category	Trademark
PrimoTek KM6075	KMI Group Inc.	PBT	PrimoTek
Mowiol® 28-99	Kuraray Co., Ltd.	PVOH	Mowiol®
Geon™ Vinyl Flexible 90049	PolyOne Corporation	PVC, Flexible	Geon™ Vinyl Flexible
MAJ'ECO EP364WF - 8229	AD majoris	PP Copolymer	MAJ'ECO
Pro-fax PL395N	INDELPRO, S.A. de C.V.	PP Homopolymer	Pro-fax

Resin Grade

Manufacturer