Polidan® EC/51
| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Polidan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2ggFO9_Polidan-EC-51.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polidan®XLPE-PEX-crosslinkable polyethylene low-density ductile polyethylene compound is moisture-crosslinkable and contains silane pre-grafted matrix compound used with catalyst masterbatch (SIOPLAS®method). standards met:-IEC 60502 XLPE, IEC 60092/351, CEI 18-16/351, BS 7655 GP8, VDE 0276 2XI1, HD 604 2XI1, |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 0.898 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 2(190°C/2.16 kg) | 0.35 | g/10 min | Internal method |
| Water absorption rate- 24 hours (100°C) | 0.600 | mg/cm² | IEC 60811 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bending test change- In the air, 240 hours (150°C) 3 | No cracking | IEC 60811 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset 4 | IEC 60811 | ||
| 250°C, maximum permanent elongation after cooling | 0.0 | % | IEC 60811 |
| 250°C, load elongation at break | 50 | % | IEC 60811 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Insulation resistance constant | IEC 60502 | ||
| 20°C | 15000 | Mohms·km | IEC 60502 |
| 90°C | 10000 | Mohms·km | IEC 60502 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Ring temperature | 170 - 190 | °C | |
| Head Temperature | 170 - 190 | °C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 868 | ||
| Shaw A | 88 | ISO 868 | |
| Shaw D | 30 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 5 | 6.10 | MPa | IEC 60811 |
| Tensile Strength (Break) | 17.0 | MPa | IEC 60811 |
| Tensile Elongation (Break) | 540 | % | IEC 60811 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| 0.5MPa, change of mechanical properties after air bomb aging test, 127°C, 40 hr | IEC 60811 | ||
| Tensile strength change | 7 | % | IEC 60811 |
| Change in tensile elongation | 6 | % | IEC 60811 |
| Changes in mechanical properties after hot air aging test, 135°C, 168 hr | IEC 60811 | ||
| Tensile strength change | 2 | % | IEC 60811 |
| Change in tensile elongation | 5 | % | IEC 60811 |
| Changes in mechanical properties after hot air aging test, 150°C, 168 hr | IEC 60811 | ||
| Tensile strength change | 9 | % | IEC 60811 |
| Change in tensile elongation | -4 | % | IEC 60811 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | IEC 60502 | ||
| 20°C | 4.1E+15 | ohms·cm | IEC 60502 |
| 90°C | 2.7E+15 | ohms·cm | IEC 60502 |
| Dielectric Strength | 35 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 2.30 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 6.0E-4 | ASTM D150 |
| Additional Information |
|---|
| 测试报告采用挤压或挤出样本获得，添加了 3% 的Catalyst CT/1，在95°C热水中交联2小时。着色 PE类母粒按重量添加 0.5-1 %；如果在存储期间吸收了水份，建议预烘干色母粒( 70-80°C下4-6小时)。 存储 产品必须按下列条件存储： --密封，包装袋完好 环境温度不超过30°C --避免在阳光下曝晒，或露天放置 存放时间过长会造成产品性状改变。 保质期： 9个月 如果没有满足上述条件，苏威特种聚合物不承担任何责任。 包装： 采用防潮袋包装。 每袋25 kg，每只货板堆放1375kg。 每只纸箱500 kg |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 140 - 160 | °C | |
| Cylinder Zone 2 Temp. | 150 - 170 | °C | |
| Cylinder Zone 3 Temp. | 160 - 180 | °C | |
| Cylinder Zone 4 Temp. | 160 - 180 | °C | |
| Die Temperature | 180 - 230 | °C |
| Extrusion instructions |
|---|
| 加工： - - POLIDAN® EC/51 预接枝基体树脂必须加用 CT/1母粒促进固化。催化剂用量为混合物重量的5％，应在挤塑加工前，2-3小时之内进行配混。 最好用挤出机料斗混合。如果催化剂用原始包装密封存储于干燥环境不需要任何预干燥。如需预干燥，可以在50-60℃温度下干燥4-8小时。 预接枝基体树脂混和物容易受潮，开袋后需在4小时内使用。预接枝基体树脂不可以预先干燥。 挤塑设备： —热塑性塑料标准挤出机，低压缩比（建议压缩比：1：1.2-1.4，L/D：25，恰当调节机筒温度，螺杆较长，需减少催化剂用量。 无需调节螺杆温度 -滤网：无 建议采用压缩装置 固化： -浸入60-70°C温水中 -暴露于环境中，交联时间取决于环境温度和相对湿度 -不管在什么情况下，固化时间都取决于保温厚度，如在温水中强行固化，壁厚 0.7-1.2 mm ，一般需要 3~6 小时。 |
| Note Message | |
|---|---|
| 1 . | 23℃ |
| 2 . | The test was performed without adding catalyst MB |
| 3 . | Untinned copper |
| 4 . | 20 N/cm² |
| 5 . | Elongation 150% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIMMA® SD6350T | Samyang Corporation | Acrylic (PMMA) | TRIMMA® |
| UNITAL® LZU | Nytef Plastics, Ltd. | Acetal (POM) Copolymer | UNITAL® |
| Generic Nylon 66/6 - Glass Fiber, Long | Generic | Nylon 66/6 | Generic |
| Oleflex™ 6261-70A-8843 Black, 307105 | Vi-Chem Corporation | TPE | Oleflex™ |
| Sylvin 2990-76 Blue 8474 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |