REXtac® APAO RT 2730
| Category: | PAO , Polyalphaolefin |
| Manufacturer: | Huntsman Corporation |
| Trademark: | REXtac® APAO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2geXfg_REXtac-APAO-RT-2730.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Butene-1 copolymer |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.870 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 0.610 | MPa | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -23.0 | °C | DSC |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Melt Density (190°C) | 0.750 | g/cm³ |
| Additional Information |
|---|
| Melt Viscosity, ASTM D3236, 250°F: 26800 cpsMelt Viscosity, ASTM D3236, 275°F: 16600 cpsMelt Viscosity, ASTM D3236, 300°F: 9600 cpsMelt Viscosity, ASTM D3236, 325°F: 6300 cpsMelt Viscosity, ASTM D3236, 350°F: 4500 cpsMelt Viscosity, ASTM D3236, 375°F: 3000 cpsMelt Viscosity, ASTM D3236, 400°F: 2400 cpsNeedle Penetration, ASTM D1321, 25°C: 2.8 mmSoftening Point by Ring and Ball, ASTM E28: 225°FShear Adhesion Failure Temp. (SAFT), Kraft/Kraft, Huntsman Method: 173°FOpen Time, Kraft/Kraft, 25°C, Huntsman Method: 120 secondsFlashpoint, COC, ASTM D93: >450°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unilex™ UP 8004 | United Polychem | PP Homopolymer | Unilex™ |
| ALTECH® PA66 A 2015/109 GF15 GN1140-13 | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| Cheng Yu FV30730 | Cheng Yu Plastic Company Limited | Acetal (POM) Homopolymer | Cheng Yu |
| Plaslube® NY-1/TF/20 NAT | Techmer Engineered Solutions | Nylon 66 | Plaslube® |
| Braskem PE GE7252XP | Braskem | HDPE | Braskem PE |