CLEAREN 530L
| Category: | SBC , Styrene Butadiene Block Copolymer |
| Manufacturer: | Denka Company Limited |
| Trademark: | CLEAREN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2gaFxg_CLEAREN-530L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CLEAREN 530L is a Styrene Butadiene Block Copolymer (SBC) product. It can be processed by injection molding and is available in Asia Pacific, Europe, or North America. Primary characteristic: high hardness. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.03 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 8.0 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 0.50 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 43.0 | MPa | |
| Break | 20.0 | MPa | |
| Nominal Tensile Strain at Break | 30 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2010 | MPa | ISO 178 |
| Flexural Stress 2 | 63.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 1.6 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 64.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 92.0 | °C | ISO 306/B |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2000 µm) | 90.0 | % | ISO 13468-1 |
| Haze (2000 µm) | 1.5 | % | ISO 14782 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 180 to 220 | °C | |
| Middle Temperature | 180 to 220 | °C | |
| Front Temperature | 180 to 220 | °C | |
| Nozzle Temperature | 190 to 200 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL NY66-G20 | Polymer Resources Ltd. | Nylon 66 | PRL |
| Hifax X M1 T05 | LyondellBasell Industries | PP Copolymer | Hifax |
| Kazan LDPE 15313-003 OKP 22 1111 2001 | Kazanorgsintez Joint Stock Company | LDPE | Kazan LDPE |
| Macromeric® 0103-212b NT | Saco Polymers | Polyolefin, Unspecified | Macromeric® |
| POLYFORT® FPP 20 GFM HI | A. Schulman Europe | PP Homopolymer | POLYFORT® |