NYLOPAK™ 570P

Category:	Nylon, Unspecified , Coextruded Nylon Film
Manufacturer:	The Dow Chemical Company
Trademark:	NYLOPAK™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	2gWlyM_NYLOPAK-570P.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
NYLOPAK 570P Coextruded Nylon Film is a multi-layer film designed for limited use protective garments. It has an outer layer of HDPE, a nylon barrier and an aggressive adhesive layer wound in. It is available as 2.0 mil, medium slip, natural color, TX, in widths from 2 to 80 inches (51 mm to 2030 mm). General Characteristics Yield: 14,300 sq in./lb (20.3 m2/kg) Thickness: 2.0 mil (51 µm) Width: 2 - 80 in. (51 - 2030 mm) Color: Natural Treat: TX (untreated) Surface Smooth Wound in: Adhesive Wound out: HDPE

General Information
Appearance	Natural Color
Forms	Film
Processing Method	Coextruded Film Extrusion Coating

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	51	µm	ASTM D374
Film Thickness - Recommended / Available	2.0 mil (51 µ)
Secant Modulus			ASTM D882
2% Secant, MD : 51 µm	303	MPa
2% Secant, TD : 51 µm	352	MPa
Tensile Strength			ASTM D882
MD : Break, 51 µm	29.6	MPa
TD : Break, 51 µm	22.1	MPa
Tensile Elongation			ASTM D882
MD : Break, 51 µm	410	%
TD : Break, 51 µm	380	%
Elmendorf Tear Strength			ASTM D1922
MD : 51 µm	130	g
TD : 51 µm	230	g
Oxygen Permeability (23°C, 51 µm, 50% RH)	3.9	cm³·mm/m²/atm/24 hr	ASTM D3985
Water Vapor Transmission Rate (38°C, 90% RH, 51 µm)	14	g/m²/24 hr	ASTM F1249
Heat Seal Strength ¹			Internal Method
MD : 177°C	960	N/m
TD : 177°C	880	N/m
Yield	20.3	m²/kg	ASTM D4321

Note Message
1 .	1 sec. preheat, 1 sec. dwell, 30 psi (2.1 bar)

Resin Grade	Manufacturer	Category	Trademark
RTP 2208 LF	RTP Company	PEEK	RTP
Sindustris PBT GP2307FI	Sincerity Australia Pty Ltd.	PBT	Sindustris PBT
Starflam EXCP0132	Eurostar Engineering Plastics	Nylon 6	Starflam
Hapflex™ 560-6	Hapco Inc.	TP, Unspecified	Hapflex™
LOXIM 100 00 V0	LOXIM Industries Private Limited	PC	LOXIM