Arlon® 37N
| Category: | PI, TP , Thermoplastic Polyimide |
| Manufacturer: | Arlon-MED |
| Trademark: | Arlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2gV8vm_Arlon-37N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 37N is a polyimide low-flow prepreg suitable for bonding multilayer polyimide rigid-flex, attaching heat sinks to polyimide MLBs, or other applications where minimal and uniform resin flow is required. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Water Absorption (24 hr) | < 1.0 | % | Internal Method |
| Decomposition Temperature | Internal Method | ||
| 5% | 340 | °C | |
| Intial | 322 | °C |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peel Strength | Internal Method | ||
| -- 1 | 1.2 | kN/m | |
| -- 2 | 0.9 | kN/m | |
| -- 3 | 1.6 | kN/m | |
| to Kapton 4 | 0.7 | kN/m |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Expansion Rate (50 to 260°C) 5 | 2.3 | % | Internal Method |
| T260 | > 1.0 | hr | Internal Method |
| T288 | 5.0 | min | Internal Method |
| T300 | 2.0 | min | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strength | 414 | MPa | Internal Method |
| Poisson's Ratio 6 | 0.17 | ASTM D3039 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 200 | °C | Internal Method |
| CLTE - Flow 7 | Internal Method | ||
| < 200°C | 7.6E-5 | cm/cm/°C | |
| > 200°C | 2.5E-4 | cm/cm/°C | |
| Thermal Conductivity (100°C) | 0.30 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | Internal Method | ||
| -- 8 | 1.2E+15 | ohms | |
| -- 9 | 4.4E+12 | ohms | |
| Volume Resistivity | Internal Method | ||
| -- 10 | 4.7E+15 | ohms·cm | |
| -- 11 | 8.2E+15 | ohms·cm | |
| Dielectric Strength | 52 | kV/mm | Internal Method |
| Dielectric Constant (1 MHz) | 4.25 | Internal Method | |
| Dissipation Factor (1 MHz) | 0.018 | Internal Method | |
| Arc Resistance | 124 | sec | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | After Thermal Stress |
| 2 . | At Elevated Temperatures |
| 3 . | After Process Solutions |
| 4 . | As Recieved |
| 5 . | Z-axis |
| 6 . | x and y direction |
| 7 . | Z-axis |
| 8 . | E24/125 |
| 9 . | C96/35/90 |
| 10 . | E24/125 |
| 11 . | C96/35/90 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Retpol® 1094 UVH | PolyPacific Pty. Ltd. | PP Copolymer | Retpol® |
| MTEGRITY™ PP Random Copolymer RP700 | M. Holland Company | PP Random Copolymer | MTEGRITY™ PP Random Copolymer |
| TRIMID® N66-G43HL | Polymer Technology and Services, LLC | Nylon 66 | TRIMID® |
| UNICAR® Unfilled PC | Nytef Plastics, Ltd. | PC | UNICAR® |
| U-polymer UM-8430RG | UNITIKA Plastics Division | Polyarylate | U-polymer |