Kingplate™ 710
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | Kingplate™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2gL8IW_Kingplate-710.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ABS710 is a plating grade ABS resin, offering high rigidity, high flow and high impact. ABS710 is recommended for automobile parts, cosmetics cases, refrigerator knobs, etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C) | 0.40 to 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 42.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 67 | % | ISO 527-2/50 |
| Flexural Modulus 1(64.0 mm) | 2190 | MPa | ISO 178 |
| Flexural Stress 2(64.0 mm) | 62.0 | MPa | ISO 178 |
| Poisson's Ratio | 0.39 | ISO 527 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179 | ||
| -30°C | 15 | kJ/m² | |
| 23°C | 30 | kJ/m² | |
| Charpy Unnotched Impact Strength 4 | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength 5 | ISO 180 | ||
| -30°C | 13 | kJ/m² | |
| 23°C | 27 | kJ/m² | |
| Unnotched Izod Impact Strength 6 | ISO 180 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 7 | |||
| 0.45 MPa, Unannealed | 85.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 75.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 95.0 | °C | ISO 306/B50 |
| CLTE | ISO 11359-2 | ||
| Flow : -40 to 40°C | 7.7E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.6E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 190 to 210 | °C | |
| Middle Temperature | 210 to 220 | °C | |
| Front Temperature | 225 to 235 | °C | |
| Nozzle Temperature | 220 to 230 | °C | |
| Processing (Melt) Temp | 220 to 230 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Back Pressure | 1.00 to 5.00 | MPa | |
| Screw Speed | 30 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Condition: 4 J |
| 4 . | Condition: 4 J |
| 5 . | Condition: 5.5 J |
| 6 . | Condition: 5.5 J |
| 7 . | 120°C/h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVALEN® PH 69 GF 30 | Plastcom | PP, Unspecified | SLOVALEN® |
| Sylvin 8327-90 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Viprene™ G85A-32U-BLK | Alliance Polymers & Services | TPV | Viprene™ |
| Beetle® PET140 | Teknor Apex Company (Chem Polymer) | PET | Beetle® |
| Sylvin 9604-90 White 1241 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |