Stanyl® TW241F12
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Stanyl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2g59cW_Stanyl-TW241F12.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Stanyl® TW241F12 is a Polyamide 46 (Nylon 46) material filled with 60% glass fiber. It is available in Asia Pacific, Europe, or North America. Important attributes of Stanyl® TW241F12 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.76 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.70 | -- | % | |
| Flow | 0.40 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.4 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| -- | 20000 | 12000 | MPa | |
| 120°C | 10000 | -- | MPa | |
| 160°C | 9100 | -- | MPa | |
| 180°C | 8500 | -- | MPa | |
| 200°C | 8000 | -- | MPa | |
| Tensile Stress | ISO 527-2 | |||
| Break | 255 | 170 | MPa | |
| Break, 120°C | 150 | -- | MPa | |
| Break, 160°C | 125 | -- | MPa | |
| Break, 180°C | 110 | -- | MPa | |
| Break, 200°C | 100 | -- | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Break | 2.0 | 3.0 | % | |
| Break, 120°C | 3.0 | -- | % | |
| Break, 160°C | 3.0 | -- | % | |
| Break, 180°C | 3.0 | -- | % | |
| Break, 200°C | 3.0 | -- | % | |
| Flexural Modulus | 17000 | 10000 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 18 | 18 | kJ/m² | |
| 23°C | 18 | 18 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 65 | 75 | kJ/m² | |
| 23°C | 90 | 100 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | 18 | 18 | kJ/m² | |
| 23°C | 18 | 18 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 290 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 295 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 2.0E-5 | -- | cm/cm/°C | |
| Transverse | 3.5E-5 | -- | cm/cm/°C | |
| Thermal Index - 5000 hr | 177 | -- | °C | IEC 60216 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flammability Classification (1.50 mm) | HB | -- | IEC 60695-11-10, -20 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 280 to 310 | °C | |
| Middle Temperature | 300 to 315 | °C | |
| Front Temperature | 300 to 315 | °C | |
| Nozzle Temperature | 300 to 310 | °C | |
| Processing (Melt) Temp | 310 to 320 | °C | |
| Mold Temperature | 60.0 to 120 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 1.00 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPV 2680 | Teknor Apex Company | TPV | Sarlink® TPV |
| Shandong Nylon A4S01 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon, Unspecified | Shandong Nylon |
| ECP 21140 | TBA Electro Conductive Products Ltd. | TPU-Polyester | ECP |
| Enviramid® N2300THL BK | Ravago Manufacturing Americas, LLC | Nylon 6 | Enviramid® |
| LNP™ KONDUIT™ PX11311 compound | SABIC Innovative Plastics Asia Pacific | Nylon 6 | LNP™ KONDUIT™ |