Toyolac® TP90-X02
| Category: | MABS , Methyl Methacrylate / ABS |
| Manufacturer: | Toray Resin Company |
| Trademark: | Toyolac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2fg32b_Toyolac-TP90-X02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Toyolac® TP90-X02 is a Methyl Methacrylate / ABS (MABS) product. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.11 | g/cm³ | ASTM D792 |
| 23°C | 1.11 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 26 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.50 to 0.70 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 40.0 | MPa | ASTM D638 |
| 23°C | 48.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 10 | % | ASTM D638 |
| Break, 23°C | 10 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 1840 | MPa | ASTM D790 |
| 23°C | 1840 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 63.0 | MPa | ASTM D790 |
| 23°C | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179 |
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.20 mm | 120 | J/m | |
| 23°C, 12.7 mm | 110 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 81.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+11 | ohms | ASTM D257 |
| Electrostatic Voltage 1(23°C) | 800 | V | Internal Method |
| Half-life of Electrostatic Voltage Decay 2(23°C) | 0.5 | sec | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (Total, 3000 µm) | 80.0 | % | ISO 13468 |
| Haze (3000 µm) | 6.0 | % | ISO 14782 |
| Note Message | |
|---|---|
| 1 . | 50%, 24 hr |
| 2 . | 50%, 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Witcom PA66 2C | Witcom Engineering Plastics B.V. | Nylon 66 | Witcom PA66 |
| Nanjing Hongrui PA66 A309 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 66 | Nanjing Hongrui PA66 |
| Estane® ETE 55DS3 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyester | Estane® |
| Fainplast PVC GS 87/BT | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Durethan® B 31 SK 000000 | LANXESS GmbH | Nylon 6 | Durethan® |