Eltex® PF1315AA
| Category: | MDPE , Medium Density Polyethylene |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | Eltex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2fbU3b_Eltex-PF1315AA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
C6 m-LLDPE for extrusion coating, injection moulding and compounding with a basic antioxidant additive package. Benefits & Features
Applications
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.914 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance (Compression Molded) | 175 | hr | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 46 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Compression Molded) | 217 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C, Compression Molded) | 9.00 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield, Compression Molded | 22 | % | |
| Break, Compression Molded | > 600 | % | |
| Flexural Modulus (23°C, Compression Molded) | 244 | MPa | ISO 178 |
| Tensile Strength at Break - Compression Molded | No Break | ISO 527-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat of Fusion | 104 | J/g | ASTM D3418 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (-20°C) | 71 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 90.0 | °C | ISO 306/A50 |
| Melting Temperature 1 | 96.0 to 114 | °C | ISO 11357-3 |
| Peak Crystallization Temperature | 84 to 100 | °C | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | < 280 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | < 280 | °C |
| Note Message | |
|---|---|
| 1 . | DSC 2nd heating, 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinkral® B 532/E | Versalis S.p.A. | ABS | Sinkral® |
| TAIRIPRO S1003 | Formosa Plastics Corporation | PP Homopolymer | TAIRIPRO |
| Vi-Chem PVC V141-70I | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Vydyne® R535J BK0678 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| UNITIKA Nylon 6 A1030BRL | UNITIKA Plastics Division | Nylon 6 | UNITIKA Nylon 6 |