AKROMID® S3 1 black (3317)
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2faHBC_AKROMID-S3-1-black-3317-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® S3 1 black (3317) is a nonreinforced and heat stabilised polyamide 6.10 with lower moisture absorption and high chemical resistance. Applications are precision parts for gears, connectors with hinges, corrugated tubes for brake boosters etc. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.08 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 10.0 | -- | cm³/10min | ISO 1133 |
| Spiral Flow | 70.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.8 | -- | % | |
| Flow | 1.6 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 1.7 | -- | % | ISO 1110 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 125 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2400 | 1200 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 70.0 | 50.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | |||
| Yield | 4.5 | 20 | % | |
| Break | > 50 | > 50 | % | |
| Flexural Modulus 1 | 1900 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 100 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.0 | -- | kJ/m² | |
| 23°C | 4.0 | 12 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | -- | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 150 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 55.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 3 | 220 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 4(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min, DSC |
| 4 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen RP348N | PolyMirae | PP Random Copolymer | Moplen |
| Wanthane® WHT-1570 | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | Wanthane® |
| Gallonprene® GP540-9005 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| INNOPOL® PP CS 1-3120 MA | Inno-Comp Ltd. | PP Homopolymer | INNOPOL® PP |
| RTP 2599 X 130537 AC-891321 COOL GREY | RTP Company | PC+ABS | RTP |