SCANLON A 5005
| Category: | ABS+Nylon , Acrylonitrile Butadiene Styrene + Nylon |
| Manufacturer: | Polykemi AB |
| Trademark: | SCANLON A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2eh26r_SCANLON-A-5005.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA/ABS-Blend |
| General Information |
|---|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.05 | -- | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (240°C/5.0 kg) | 7.5 | -- | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.90 | -- | % | |
| Flow | 0.90 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 64 | -- | ASTM D2240 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress | 40.0 | 35.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 150 | > 200 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 1400 | 1200 | MPa | ISO 178 |
| Flexural Stress | 50.0 | 45.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -20°C | -- | 25 | kJ/m² | |
| 23°C | 45 | 50 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 1 | ||||
| 0.45 MPa, Unannealed | 90.0 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 60.0 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | ||||
| -- | 185 | -- | °C | ISO 306/A50 |
| -- | 105 | -- | °C | ISO 306/B50 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 650 | -- | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® PSC 6020 | Marco Polo International, Inc. | PS (GPPS) | MARPOL® PSC |
| Qenos PE HD1090 | Qenos Pty Ltd | HDPE | Qenos PE |
| Talcoprene® 1040TC NAT | SO.F.TER. SPA | PP Homopolymer | Talcoprene® |
| Topilene® J842 | Hyosung Corporation | PP Impact Copolymer | Topilene® |
| ALTECH® PA66 A 2035/508 GF35 | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |