Marlex® HMN TR-942G

Wechat: WECHAT

Message
These hexene copolymers are tailored for rotational molding applications that require: Wide process windows Excellent impact strength Good flow Good ESCR These resins are available in: Pellet form - HMN TR-942 35 US mesh powder - HMN TR-942G Typical applications for HMN TR-942 and HMN TR-942G include items such as: Potable water and chemical tanks Agricultural equipment These resins meet these specifications: ASTM D4976 - PE 233 FDA 21 CFR 177.1520(c) 3.2a, use conditions B through H per 21 CFR 176.170(c) Table 2. Single use articles contacting food types I, II, IV-B, VI-A, VI-B, VII-B, and VIII. Repeated use articles contacting all food types defined in 21 CFR 176.170(c) Table 1. FMVSS.302 burn test NSF / ANSI Standard 61 for potable water (CLD 23) Long term UV stabilization - ASTM 2565 (Cycle 1): Greater than UV-16

Message

These hexene copolymers are tailored for rotational molding applications that require:

These resins are available in:

Typical applications for HMN TR-942 and HMN TR-942G include items such as:

These resins meet these specifications:

FDA 21 CFR 177.1520(c) 3.2a, use conditions B through H per 21 CFR 176.170(c) Table 2. Single use articles contacting food types I, II, IV-B, VI-A, VI-B, VII-B, and VIII. Repeated use articles contacting all food types defined in 21 CFR 176.170(c) Table 1.

General Information
Additive	UV stabilizer
Features	High ESCR (Stress Cracking Resistance) hexene comonomer Impact resistance, good Good UV resistance Good liquidity
Uses	Agricultural application Water tank
Agency Ratings	ASTM D 2565 ASTM D 4976-PE233 FDA 21 CFR 177.1520(c) 3.2a 2 NSF 61
Forms	Powder
Processing Method	rotomolding

Physical	Nominal Value	Unit	Test Method
Density	0.943	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	2.0	g/10 min	ASTM D1238
Environmental Stress-Cracking Resistance			ASTM D1693A
10% Igepal, molded, F50	250	hr	ASTM D1693A
100% Igepal, molded, F50	700	hr	ASTM D1693A

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D, Compression Molded)	61		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹(Yield, 3.17 mm, Rotational Molded)	21.0	MPa	ASTM D638
Tensile Elongation ²(Break, 3.17 mm, Rotational Molded)	720	%	ASTM D638
Flexural Modulus ³			ASTM D790
2% positive cut : mm, rotational molding	720	MPa	ASTM D790
Tangent : mm, rotational molding	860	MPa	ASTM D790

Impact	Nominal Value	Unit
ARM Impact
-40°C, 3.20 mm	92.0	J
-40°C, 6.35 mm	244	J

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, unannealed, 3.17mm, rotational molding	64.0	°C	ASTM D648
1.8 MPa, unannealed, 3.17mm, rotational molding	44.0	°C	ASTM D648
Brittleness Temperature	-75.0	°C	ASTM D746A
Vicat Softening Temperature	120	°C	ASTM D1525 ⁴
Peak Melting Temperature	130	°C	ASTM D3418
Peak Crystallization Temperature (DSC)	113	°C	ASTM D3418

Resin Grade	Manufacturer	Category	Trademark
RTP 200.6	RTP Company	Nylon 66	RTP
Radilon® S RV350 100 NAT	Radici Plastics	Nylon 6	Radilon®
Telcar® TL-2522C	Teknor Apex Company	TPE	Telcar®
Grilamid® LBV-50H FWA nat	EMS-GRIVORY	Nylon 12	Grilamid®
Hylon® N4033HL	Ravago Manufacturing Americas, LLC	Nylon 66/6	Hylon®

Resin Grade

Manufacturer

Category:	HDPE , High Density Polyethylene
Manufacturer:	Chevron Phillips Chemical Company LLC
Trademark:	Marlex®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	2eSEkQ_MarlexHMNTR942G.pdf
PRICE:	Order Products email sales@su-jiao.com