| 30% glass fiber reinforced and impact modified Polyamide 612 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.26 | g/cm³ | ISO 1183/A |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 120 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.8 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1(23°C) | 6000 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 150 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength (23°C) | 3.20 | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 10 | kJ/m² | |
| 23°C | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 50 | kJ/m² | |
| 23°C | 60 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 195 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 185 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 210 | °C | ISO 306/A50 |
| -- | 165 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (2.00 mm) | < 100 | mm/min | ISO 3795 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ PD 40 TF Black | PolyOne Corporation | PP Homopolymer | Maxxam™ |
| Next Nylon 66 Prime Series PXHS-01NC | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| NOVA ABS 780 NAT | NOVA Polymers, Inc. | ABS | NOVA ABS |
| EVALENE® HDPE HF14522 | JG Summit Petrochemical Corporation | HDPE | EVALENE® HDPE |
| Metocene MF650X | LyondellBasell Industries | PP Homopolymer | Metocene |