FORMULA P COMP 3220
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Putsch Kunststoffe GmbH |
| Trademark: | FORMULA P |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2bPQSe_FORMULA-P-COMP-3220.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene, with 20% Talc reinforcement. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 17 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.0 - 1.2 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 29.0 | MPa | ISO 527-2 |
| Fracture | 18.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 50 | % | ISO 527-2 |
| Flexural Modulus | 2700 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 60.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180 | ||
| -20°C | 1.0 | kJ/m² | ISO 180 |
| 23°C | 2.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 98.0 | °C | ISO 306/B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 13 | mm/min | VW TL1010 |
| Additional Information |
|---|
| Tensile Strength, ISO 527: 29 MPa |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 220 - 255 | °C | |
| Mold Temperature | 20.0 - 40.0 | °C |
| Injection instructions |
|---|
| Drying Not Required |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Witcom PPS 2006/351 | Witcom Engineering Plastics B.V. | PPS | Witcom PPS |
| Novalloy-B B4720 | PlastxWorld Inc. | ABS+PBT | Novalloy-B |
| AKROMID® B3 GF 30 1 L black (4365) | AKRO-PLASTIC GmbH | Nylon 6+PP | AKROMID® |
| KRYSTALFLEX™ PE501 | Huntsman Corporation | PUR-Eth,aliphat | KRYSTALFLEX™ |
| Polychim HB12XF | Polychim Industrie S.A.S. | PP Homopolymer | Polychim |