ADENE NCZB
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | A.D. Compound spa |
| Trademark: | ADENE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2aX8Tq_ADENE-NCZB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ADENE NCZB is a Polypropylene Homopolymer (PP Homopolymer) material filled with 70% calcium carbonate. It is available in Europe or North America. Primary attribute of ADENE NCZB: Homopolymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.68 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Ash Content | 70 | % | ISO 3451-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 14.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 4.0 | % | |
| Break | 8.0 | % | |
| Flexural Modulus | 4900 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 2.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 5.0 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 71.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 106 | °C | ISO 306/B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SI-LINK™ AC DFDB-5451 NT | The Dow Chemical Company | PE, Unspecified | SI-LINK™ |
| Addisil™ 470 E | Momentive Performance Materials Inc. | Rubber | Addisil™ |
| Electrafil® ABS CF15 BK | Techmer Engineered Solutions | ABS | Electrafil® |
| Hylon® N2000STHL | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |
| Sylvin 8200-80UV Red 6257 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |