AVP™ ZLL19CP
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | AVP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2ZecOZ_AVP-ZLL19CP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| AVP™ ZLL19CP is a Polycarbonate (PC) product. It can be processed by injection molding and is available in North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 19 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.18 mm) | 56.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.18 mm) | 50 | % | ASTM D638 |
| Flexural Modulus 3(3.18 mm) | 2210 | MPa | ASTM D790 |
| Flexural Strength 4(3.18 mm) | 86.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reverse Notch Izod Impact (23°C, 3.18 mm) | 2100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm) | 127 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-2 | ||
| 3.00 mm | V-1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 | hr | |
| Drying Time, Maximum | 16 | hr | |
| Rear Temperature | 282 to 293 | °C | |
| Middle Temperature | 288 to 316 | °C | |
| Front Temperature | 288 to 316 | °C | |
| Nozzle Temperature | 288 to 316 | °C | |
| Processing (Melt) Temp | 299 to 327 | °C | |
| Mold Temperature | 82.2 to 116 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| GAPEX® FPP30RA05WH | Ferro Corporation | PP, Unspecified | GAPEX® |
| Elastron® V P.V101.A50.B | Elastron USA, Inc. | TPV | Elastron® V |
| Mafill® CR XT 6341 | Ravago Group | PP, Unspecified | Mafill® |
| PLEXIGLAS® Film White WF007 | Evonik Industries AG | Film, PMMA | PLEXIGLAS® Film |
| Osterlene® LLB0918A | Osterman & Company | LLDPE | Osterlene® |