NORYL™ HS2000X resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2WvuGA_NORYL-HS2000X-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PPE+PS blend. 17% Mineral reinforced. Non-brominated, non-chlorinated FR system. UL94 V0 and 5VA listing. UL746C f1. Radiant panel listing. Dielectric strength. Dimensional stability. Suitable for E/E market indoor/outdoor applications including electrical ceiling boxes and smoke detectors. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 280°C/5.0 kg | 7.6 | g/10 min | |
| 300°C/5.0 kg | 7.6 | g/10 min | |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 280°C/5.0 kg | 6.80 | cm³/10min | |
| 300°C/5.0 kg | 6.80 | cm³/10min | |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Outdoor Suitability | f1 | UL 746C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3650 | MPa | ASTM D638 |
| -- | 4000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 74.0 | MPa | ASTM D638 |
| Yield | 71.7 | MPa | ISO 527-2 |
| Break 3 | 60.0 | MPa | ASTM D638 |
| Break | 57.1 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 3.8 | % | ASTM D638 |
| Yield | 3.7 | % | ISO 527-2 |
| Break 4 | 8.4 | % | ASTM D638 |
| Break | 11 | % | ISO 527-2 |
| Flexural Modulus | |||
| 100 mm Span 5 | 3550 | MPa | ASTM D790 |
| 50.0 mm Span 6 | 3670 | MPa | ASTM D790 |
| -- | 3800 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 117 | MPa | ISO 178 |
| Yield, 100 mm Span 7 | 117 | MPa | ASTM D790 |
| Break, 50.0 mm Span 8 | 117 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/2C |
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| 23°C 9 | 9.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 2200 | J/m | ASTM D4812 |
| Reverse Notch Izod Impact (3.20 mm) | 810 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Total Energy) | 443 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 117 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 6.40 mm | 128 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 100 mm Span 10 | 126 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 3.20 mm | 108 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 6.40 mm | 116 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 100 mm Span 11 | 111 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 132 | °C | ISO 306/B50 |
| -- | 136 | °C | ISO 306/B120 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 7.1E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.8E-5 | cm/cm/°C | |
| RTI Elec | 100 | °C | UL 746 |
| RTI Imp | 85.0 | °C | UL 746 |
| RTI Str | 100 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.2E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.20 mm, in Oil) | 17 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 2.89 | ||
| 60 Hz | 2.89 | ||
| 1 MHz | 2.70 | ||
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 0.017 | ||
| 60 Hz | 0.017 | ||
| 1 MHz | 4.4E-3 | ||
| Arc Resistance 12 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 2 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.47 mm | V-0 | ||
| 2.01 mm | 5VA | ||
| Radiant Panel Listing (UL) | YES |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 70 | % | |
| Rear Temperature | 249 to 299 | °C | |
| Middle Temperature | 260 to 304 | °C | |
| Front Temperature | 271 to 310 | °C | |
| Nozzle Temperature | 282 to 310 | °C | |
| Processing (Melt) Temp | 282 to 310 | °C | |
| Mold Temperature | 76.7 to 104 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 20 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | 2.6 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.6 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 120*10*4 mm |
| 11 . | 120*10*4 mm |
| 12 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecomid® NB40 NL IH | Eurotec Engineering Plastics | Nylon 6 | Tecomid® |
| Sinvicomp SSG7006 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| VITAMIDE® BW34BK6358 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| PIVINEL™ PROD-1 | HELLENIC CABLES S.A. | PVC, Unspecified | PIVINEL™ |
| StarFlex® 7393-1002 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarFlex® |