Stanyl® TS350
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Stanyl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2WvVeq_Stanyl-TS350.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Stanyl® TS350 is a Polyamide 46 (Nylon 46) material. It is available in Asia Pacific. Important attributes of Stanyl® TS350 are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.43 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.5 | -- | % | |
| Flow | 1.5 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.4 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3400 | -- | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 80.0 | -- | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 7.0 | -- | % | ISO 527-2 |
| Flexural Modulus | 3200 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 3.0 | -- | kJ/m² | |
| 23°C | 4.0 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 190 | -- | °C | ISO 75-2/A |
| Melting Temperature | 295 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 8.0E-5 | -- | cm/cm/°C | |
| Transverse | 9.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+9 | ohms·cm | IEC 60093 |
| Electric Strength | 30 | 25 | kV/mm | IEC 60243-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.750 mm | V-0 | -- | ||
| 1.50 mm | V-0 | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 280 to 320 | °C | |
| Middle Temperature | 300 to 320 | °C | |
| Front Temperature | 300 to 320 | °C | |
| Nozzle Temperature | 300 to 320 | °C | |
| Processing (Melt) Temp | 310 to 320 | °C | |
| Mold Temperature | 80.0 to 120 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 2.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ NR-818.H001-8086 | PolyOne Corporation | PP, Unspecified | Maxxam™ |
| T-Blend® 6594B-WGL60 | TSRC Corporation | SEBS | T-Blend® |
| NYLOY® MG-0235B-2 | Nytex Composites Co., Ltd. | Nylon 66 | NYLOY® |
| AIE PA66 60G3F | Asia International Enterprise (Hong Kong) Limited | Nylon 66 | AIE PA66 |
| Jam HDPE HH4765 | Jam Petrochemical Company | HDPE | Jam HDPE |