Lumid® HI5006A(W)
| Category: | Nylon 6+ABS , Polyamide 6 + ABS |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lumid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2WcBCp_Lumid-HI5006A-W-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description High Impact, Good Dimensional Stability Application Pipe Fitting , Electrical and Electronic parts |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (23°C, 3.20 mm) | 0.80 to 1.2 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.70 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 44.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 100 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 1570 | MPa | ASTM D790 |
| Flexural Strength 4(6.40 mm) | 59.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.40 mm) | 690 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 110 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 80.0 | °C | |
| Peak Melting Temperature | 220 | °C | ASTM D3418 |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C, 1.00 mm) | 26 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C, 1 MHz) | 2.90 | ASTM D150 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 90.0 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Rear Temperature | 235 to 250 | °C | |
| Middle Temperature | 240 to 260 | °C | |
| Front Temperature | 240 to 260 | °C | |
| Nozzle Temperature | 250 to 265 | °C | |
| Processing (Melt) Temp | 250 to 265 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 3.0 mm/min |
| 4 . | 3.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 2308AN00 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| X-Pro SP 200 TF 30 3033 | CTC Plastics, LLC | PP, Unspecified | X-Pro |
| EMOPLEN® A 1104 T4 | EMAS Plastik San.Tic.AS. | PP, Unspecified | EMOPLEN® |
| INEOS HDPE T50-500-196 | INEOS Olefins & Polymers USA | HDPE Copolymer | INEOS HDPE |
| Plaskon S-7PG | Cookson Electronics - Semiconductor Products | Epoxy | Plaskon |